Objectives: This study evaluated the effects of the resin thickness on the microhardness and optical properties of bulk-fill resin composites. Materials and Methods: Four bulk-fill (Venus Bulk Fill, Heraeus Kulzer; SDR, Dentsply Caulk; Tetric N-Ceram Bulk Fill, Ivoclar vivadent; SonicFill, Kerr) and...
Objectives: This study evaluated the effects of the resin thickness on the microhardness and optical properties of bulk-fill resin composites. Materials and Methods: Four bulk-fill (Venus Bulk Fill, Heraeus Kulzer; SDR, Dentsply Caulk; Tetric N-Ceram Bulk Fill, Ivoclar vivadent; SonicFill, Kerr) and two regular resin composites (Charisma flow, Heraeus Kulzer; Tetric N-Ceram, Ivoclar vivadent) were used. Sixty acrylic cylindrical molds were prepared for each thickness (2, 3 and 4 mm). The molds were divided into six groups for resin composites. The microhardness was measured on the top and bottom surfaces, and the colors were measured using Commission Internationale d'Eclairage (CIE) $L^*a^*b^*$ system. Color differences according to the thickness and translucency parameters and the correlations between the microhardness and translucency parameter were analyzed. The microhardness and color differences were analyzed by ANOVA and Scheffe's post hoc test, and a student t-test, respectively. The level of significance was set to ${\alpha}=0.05$. Results: The microhardness decreased with increasing resin thickness. The bulk-fill resin composites showed a bottom/top hardness ratio of almost 80% or more in 4 mm thick specimens. The highest translucency parameter was observed in Venus Bulk Fill. All resin composites used in this study except for Venus Bulk Fill showed linear correlations between the microhardness and translucency parameter according to the thickness. Conclusions: Within the limitations of this study, the bulk-fill resin composites used in this study can be placed and cured properly in the 4 mm bulk.
Objectives: This study evaluated the effects of the resin thickness on the microhardness and optical properties of bulk-fill resin composites. Materials and Methods: Four bulk-fill (Venus Bulk Fill, Heraeus Kulzer; SDR, Dentsply Caulk; Tetric N-Ceram Bulk Fill, Ivoclar vivadent; SonicFill, Kerr) and two regular resin composites (Charisma flow, Heraeus Kulzer; Tetric N-Ceram, Ivoclar vivadent) were used. Sixty acrylic cylindrical molds were prepared for each thickness (2, 3 and 4 mm). The molds were divided into six groups for resin composites. The microhardness was measured on the top and bottom surfaces, and the colors were measured using Commission Internationale d'Eclairage (CIE) $L^*a^*b^*$ system. Color differences according to the thickness and translucency parameters and the correlations between the microhardness and translucency parameter were analyzed. The microhardness and color differences were analyzed by ANOVA and Scheffe's post hoc test, and a student t-test, respectively. The level of significance was set to ${\alpha}=0.05$. Results: The microhardness decreased with increasing resin thickness. The bulk-fill resin composites showed a bottom/top hardness ratio of almost 80% or more in 4 mm thick specimens. The highest translucency parameter was observed in Venus Bulk Fill. All resin composites used in this study except for Venus Bulk Fill showed linear correlations between the microhardness and translucency parameter according to the thickness. Conclusions: Within the limitations of this study, the bulk-fill resin composites used in this study can be placed and cured properly in the 4 mm bulk.
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
문제 정의
Also, there are few reports of the microhardness and optical properties according to resin thickness of these composites. Therefore, this study investigated the effects of the resin thickness on the microhardness and optical properties of bulk-fill resin composites.
대상 데이터
Four bulk-fill resin composites (Venus Bulk Fill, VB; SDR, SR; Tetric N-Ceram Bulk Fill, TB; SonicFill, SO) and two regular resin composites (Charisma flow, CF; Tetric N-Ceram, TN) were used. CF was used as the control group of flowable bulk-fill resin composites including VB and SR, whereas TN was used as the control group of the non-flowable bulk-fill resin composites including TB and SO.
Sixty acrylic cylindrical molds with a socket, 9 mm in diameter, were prepared for each thickness (2 mm, 3 mm and 4 mm). They were divided into six groups for each resin composite (n = 10).
데이터처리
*Student t-test.
The microhardness was analyzed by one-way and two-way ANOVA and Scheffe’s post hoc test, and the color differences were analyzed using a student t-test. TP was analyzed by one-way ANOVA. The software used was SPSS 15.
The microhardness was analyzed by one-way and two-way ANOVA and Scheffe’s post hoc test, and the color differences were analyzed using a student t-test.
성능/효과
For the restorations with bulk-fill resin composites, the manufacturers recommend that 4 mm thick increments can be cured in a single step. Based on the results of this study, up to 4 mm thick increments of bulk-fill resin composites are clinically acceptable.
05). Furthermore, the percentage of the bottom to top surface hardness (bottom/top hardness ratio) of the 4 mm specimens for VB, SR, CF, TB, SO, and TN were 94.2%, 87.3%, 60.4%, 78.7%, 84.8% and 52.4%, respectively. The bulk-fill resin composite groups including VB, SR, SO and TB showed a bottom/top hardness ratio of almost 80% or more in the 4 mm thick specimens.
참고문헌 (19)
1 Lassila LV Nagas E Vallittu PK Garoushi S Translucency of flowable bulk-filling composites of various thickness Chin J Dent Res 2012 15 31 35 22866280
2 Ilie N Bucuta S Draenert M Bulk-fill resin-based composites: an in vitro assessment of their mechanical performance Oper Dent 2013 38 618 625 23570302
3 Czasch P Ilie N In vitro comparison of mechanical properties and degree of cure of bulk fill composites Clin Oral Investig 2013 17 227 235
4 Ilie N Keßler A Durner J Influence of various irradiation processes on the mechanical properties and polymerisation kinetics of bulk-fill resin based composites J Dent 2013 41 695 702 23707645
5 Flury S Hayoz S Peutzfeldt A Hüsler J Lussi A Depth of cure of resin composites: is the ISO 4049 method suitable for bulk fill materials? Dent Mater 2012 28 521 528 22391146
6 Tanthanuch S Ruenqsri P Kukiattrakoon B Optimal depth of cure for nanohybrid resin composite using quartz tungsten halogen and new high intensity lightemitting diode curing units Gen Dent 2013 61 e14 e17 23928448
7 Finan L Palin WM Moskwa N McGinley EL Fleming GJ The influence of irradiation potential on the degree of conversion and mechanical properties of two bulk-fill flowable resin composite base materials Dent Mater 2013 29 906 912 23787035
8 Price RB Dérand T Loney RW Andreou P Effect of light source and specimen thickness on the surface hardness of resin composites Am J Dent 2002 15 47 53 12074230
9 Ilie N Hickel R Investigations on a methacrylate-based flowable composite based on the SDR™ technology Dent Mater 2011 27 348 355 21194743
10 Bouschlicher MR Rueggeberg FA Wilson BM Correlation of bottom-to-top surface microhardness and conversion ratios for a variety of resin composite compositions Oper Dent 2004 29 698 704 15646227
11 Moore BK Platt JA Borges G Chu TM Katsilieri I Depth of cure of dental resin composites: ISO 4049 depth and microhardness of types of materials and shades Oper Dent 2008 33 408 412 18666498
16 Kim IJ Lee YK Changes in color and color parameters of dental resin composites after polymerization J Biomed Mater Res B Appl Biomater 2007 80 541 546 16924627
17 Lee YK Influence of filler on the difference between the transmitted and reflected colors of experimental resin composites Dent Mater 2008 24 1243 1247 18343494
※ AI-Helper는 부적절한 답변을 할 수 있습니다.