[논문]3종의 간접수복용 복합레진의 굴곡강도 비교 및 표면관찰

김준태; 박진영; 김웅철; 김지환

doi:10.14347/kadt.2017.39.1.9

3종의 간접수복용 복합레진의 굴곡강도 비교 및 표면관찰
Evaluation of Flexural strength and surface porosity of three indirect composite resins 원문보기

대한치과기공학회지 = The Journal of Korean Academy of Dental Technology, v.39 no.1, 2017년, pp.9 - 16

김준태 (고려대학교 대학원 보건과학과 치의기공전공) , 박진영 (고려대학교 보건과학연구소) , 김웅철 (고려대학교 대학원 보건과학과 치의기공전공) , 김지환 (고려대학교 대학원 보건과학과 치의기공전공)

Abstract ▼ AI-Helper

Purpose: The purpose of this study was to evaluate flexural strength, composite surface and fractured surface of three different indirect composite resins. Methods: Fifteen bar-shaped specimens ($25mm{\times}2mm{\times}2mm$) were fabricated for each FL group (Flow type and Light curing) and PLP group (Putty type and Light, Pressure curing) and PL group (Putty type and Light curing) according to manufacturer's instructions and ISO 10477. Fabricated specimens were stored in the distilled water for 24 hours at the temperature of $37^{\circ}C$. Three-point bending strength test was performed to measure flexural strength using universal testing machine at a crosshead speed of 1mm/min (ISO 10477). Surface and fractured surface of specimens were observed by digital microscope. Results were analyzed with Kruskal-wallis tests (${\alpha}=0.05$). Results: Mean (SD) of three different indirect composite resins were 83.38 (6.67) MPa for FL group, 139.90(16.53) MPa for PLP group and 171.72(16.74) MPa for PL group. Flexural strength were statistically significant (p<0.05). Differences were not observed at fractured surface among three groups. However, many pores over $100{\mu}m$ were observed at PL group in observing surface of specimen. Conclusion: Flexural strength of composite resins was affected by second polymerization method and content of inorganic filler.

주제어

AI 본문요약
AI-Helper

문제 정의

하지만 임상에서 적용되고 있는 간접수복용 복합레진의 종류가 다양하고 중합방법 또한 차이가 있음에도 불구하고 이에 대한 연구가 미흡한 실정이다. 따라서 본 연구의 목적은 3종의 간접수복용 복합레진의 굴곡강도를 비교하고, 표면관찰을 통하여 기포의 함유 정도를 확인함으로써 각각 재료들의 임상적용을 위한 가이드를 제시하고자 한다.

제안 방법

굴곡강도의 측정을 위하여 국제표준규격(ISO 10477)(DIN 2004)에 근거하여 길이 25mm, 폭 2mm, 두께 2mm의 막대모양 시편을 제작하였다. 시편을 제작하기 위하여 규격에 맞게 설계된 Teflon mold에 제작된 Teflon zig에 복합레진을 전입하고 기포의 함입을 차단하기 위하여 레진의 위/아래에 플라스틱 비닐을 위치시킨 후, 유리판을 이용해 압접을 시행하였다(Fig 1).
굴곡강도의 측정을 위하여 국제표준규격(ISO 10477)(DIN 2004)에 근거하여 길이 25mm, 폭 2mm, 두께 2mm의 막대모양 시편을 제작하였다. 시편을 제작하기 위하여 규격에 맞게 설계된 Teflon mold에 제작된 Teflon zig에 복합레진을 전입하고 기포의 함입을 차단하기 위하여 레진의 위/아래에 플라스틱 비닐을 위치시킨 후, 유리판을 이용해 압접을 시행하였다(Fig 1). 이후 압접으로 인하여 발생된 여분의 복합레진을 제거한 후 각각 제조사의 중합법에 따라 중합을 진행하였다.
파절면 및 표면은 굴곡강도 측정 후 발생된 시편의 파편을 이용하여 관찰하였다. 파절 후 발생된 시편의 파절면은 15개의 시편 중 임의로 선택하여 디지털 현미경(KH-7700, HITOX, Japan)으로 140배 확대하여 관찰하였고, 시편의 표면은 120배로 확대하여 관찰하였다.

대상 데이터

본 연구에서는 임상에서 사용되는 3종의 복합레진인Sinfony, Tescera, Twiny을 사용하였다(Table 1)

데이터처리

굴곡강도의 기술통계는 평균과 표준편차로 나타내었고 정규성 분포 가정을 만족하지 못하였다(p<0.05). 따라서 복합레진의 종류에 따른 굴곡강도의 차이를 평가하기 위하여 비모수 검정인 Kruskal-wallis test를 시행하였다.
05). 따라서 복합레진의 종류에 따른 굴곡강도의 차이를 평가하기 위하여 비모수 검정인 Kruskal-wallis test를 시행하였다. 통계적 판단을 위하여 통계적 유의수준은 0.

이론/모형

제조사의 지시대로 제작된 시편들은 만능재료 시험기(Instron 3345; Instron, Canton, MA, USA)를 이용하여 3점 굽힘시험법으로 굴곡강도를 측정하였다. 하중속도는 1.

성능/효과

1. ISO 10477 규격에 따라 실험한 복합레진의 굴곡강도는 PL군에서 가장 높게 나타났고 PLP군, FL군 순으로 나타났다(p<0.05).
3. 디지털 현미경으로 관찰한 복합레진의 표면에서 PLP군과 FL군에서는 큰 차이를 관찰할 수 없었지만, PL군에서는 100㎛이상의 큰 기포를 다수 관찰할 수 있었다.
이는 굴곡강도가 함량의 비율 순과 비례한다고 볼 수 있으며, FL이 가장 낮은 굴곡강도를 보인 것은 PL군과 PLP군과 다르게 광중합만을 한 중합방법의 차이로 나타났다. 따라서 간접수복용 복합레진으로는 우수한 굴곡강도를 나타낸 PL 그룹의 적용을 권장하고, 추후 표면 기포를 제거할 수 있도록 후 처리가 필요할 것으로 사료된다.

후속연구

이는 굴곡강도가 함량의 비율 순과 비례한다고 볼 수 있으며, FL이 가장 낮은 굴곡강도를 보인 것은 PL군과 PLP군과 다르게 광중합만을 한 중합방법의 차이로 나타났다. 따라서 간접수복용 복합레진으로는 우수한 굴곡강도를 나타낸 PL 그룹의 적용을 권장하고, 추후 표면 기포를 제거할 수 있도록 후 처리가 필요할 것으로 사료된다.
특히 PL 그룹에서는 제조사에서 제시한 굴곡강도 240에 크게 밑돌았는데 이는 PL를 독점으로 수입하고 있는 재료상에서 수입단가와 국내 시장가격을 고려하여 PL 제조사의 열중합기가 아닌, 자체적으로 제작한 열중합기를 제공하고 있기 때문에 이를 기초로 실험을 진행하여 발생된 오차일 것으로 생각된다. 또한 기포를 다량 함유하고 있음에도 불구하고 PL그룹에서 가장 높은 굴곡강도를 나타냈다는 점 또한 추후 연구가 필요할 것으로 보인다.

질의응답

핵심어	질문	논문에서 추출한 답변
	대표적인 치과용 심미수복재는?	구강 내 기능 회복을 우선으로 하던 과거와 달리, 사회/경제가 발전함에 따라 환자들의 요구가 증가됨으로써 치아색조와 관련된 재료들의 개발과 발전이 이루어지고 있다. 대표적인 치과용 심미수복재는 글레스아이오노머, 복합레진 그리고 세라믹 등이 있다. 이 중에서 복합레진은 높은 중합수축으로 인하여 미세누출을 야기하고 이로 인해 2차 우식증을 유발시키는 문제점이 있었다(Thordrup et al, 1994).
	복합레진의 문제점은?	대표적인 치과용 심미수복재는 글레스아이오노머, 복합레진 그리고 세라믹 등이 있다. 이 중에서 복합레진은 높은 중합수축으로 인하여 미세누출을 야기하고 이로 인해 2차 우식증을 유발시키는 문제점이 있었다(Thordrup et al, 1994). 또한 우수한 마모저항성과 기계적 성질을 요구하는 구치부수복에 한계가 있다(강현숙 and 최호영).
	복합레진의 가진 한계는?	이 중에서 복합레진은 높은 중합수축으로 인하여 미세누출을 야기하고 이로 인해 2차 우식증을 유발시키는 문제점이 있었다(Thordrup et al, 1994). 또한 우수한 마모저항성과 기계적 성질을 요구하는 구치부수복에 한계가 있다(강현숙 and 최호영). 따라서 구강 외에서 중합 및 제작을 통하여 우수한 적합도와 강도, 마모저항성을 가진 복합레진 인레이에 대한 개념이 도입되었다(Leinfelder1988; Hasegawa et al, 1989).

참고문헌 (32)

Asmussen E. Restorative resins: hardness and strength vs. quantity of remaining double bonds. Eur J Oral Sci, 90(6), 484-489, 1982.

상세보기
Bertolotti RL. A new polymer glass utilized for modification and repair of fixed partial dentures. Quintessence Int 28(7), 437-439, 1997.
Callaghan DJ, Vaziri A, Nayeb-Hashemi H. Effect of fiber volume fraction and length on the wear characteristics of glass fiberreinforced dental composites. Dent Mater, 22(1), 84-93, 2006.

상세보기
Chee WW, Donovan TE, Daftary F, Siu T. The effect of vacuum-mixed autopolymerizing acrylic resins on porosity and transverse strength. J Prosthet Dent, 60(4), 517-519, 1988.

상세보기
Condon JJ. Ferracane. In vitro wear of composite with varied cure, filler level, and filler treatment. J Dent Res, 76(7), 1405-1411, 1997.

상세보기
Cook WD, Johannson M. The influence of postcuring on the fracture properties of photo-cured dimethacrylate based dental composite resin. J Biomed Mater Res A, 21(8), 979-989, 1987.

상세보기
DIN E. 1 0477, Dentistry-Polymer-based crown and bridge materials, Beuth Verlag, Berlin, 2004.
Ferracane J, Condon J. Post-cure heat treatments for composites: properties and fractography. Dent Mater, 8(5), 290-295, 1992.

상세보기
Freiberg R, Ferracane J. Evaluation of cure, properties and wear resistance of Artglass dental composite. Am J Dent, 11(5), 214-218, 1998.

상세보기
Geum YH, Kim B. Flexural strength of indirect compositeresin wi th different polymerization conditions. J Kor Aca Dent Tec, 35(4), 333-341, 2013.

원문보기 상세보기
Hasegawa E, Boyer D, Chan DC. Microleakage of indirect composite inlays. Dent Mater, 5(6), 388-391, 1989.

상세보기
Ho CT, Vijayaraghavan T, Lee SY, Tsai A, Huang HM, Pan LC. Flexural behaviour of post -cured composites at oral-simulating temperatures. J Oral Rehabil, 28(7), 658-667, 2001.

상세보기
Ikejima I , Nomoto R, McCabe JF. Shear punch strength and flexural strength of model composites with varying filler volume fraction, particle size and silanation. Dent Mater, 19(3), 206-211, 2003.

상세보기
Inoue K, Terachi M, Utsumi S. A study on composite resin inlay. J Dent Res, 67, 222, 1988.
ISO, E . 4049, Dentistry-Polymer-based filling, restorative and luting materials. International Organization for Standardization, Geneva, Switzerland, 1988.
Jun SK , Kim DA, Goo HJ, Lee HH. Investigation of the correlation between the different mechanical properties of resin composites. Dent Mater J, 32(1), 48-57, 2013.

상세보기
Junior SAR, Ferracane JL, Della Bona A. Flexural strength and Weibull analysis of a microhybrid and a nanofill composite evaluated by 3-and 4-point bending tests. Dent Mater, 24(3), 426-431, 2008.

상세보기
Kim KS, Yoon TH, Song KY, Ahn SG. Comparison of mechanical properties in 4 indirect composite resin. J Korean Acad Prosthodont, 45(1), 21-33, 2007.
Leinfel der KF. Posterior composite resins. J Am Dent Accoc, 117(4), 21E-26E, 1988.

상세보기
Shinkai MN, McGivney GP, Davis E, Bush PJ, Carter JM. A comparison of the wear resistance and hardness of indirect composite resins. J Prosthet Dent, 85(4), 386-395,2001.

상세보기
Neves AD, Discacciati JAC, Orefice RL, Jansen WC. Correlation between degree of conversion, microhardness and inorganic content in composites. Braz Oral Res, 16(4): 349-354, 2002.
Optec H. Laboratory techniques manual. Wallingford, Conn: Jeneric/Pentron, l-24.
Reinhardt JW, Boyer D, Stephens N. Effects of secondary curing on indirect posterior composite resins. Oper Dent, 19, 217-217, 1994.

상세보기
Satsukawa H, Koizumi H, Tanoue N, Nemoto M, Ogino T, Matsumura H. Properties of an indirect composite material polymerized with two different laboratory polymerizing systems. Dent Mater J, 24(3), 377-381, 2005.

상세보기
Shinka i K, Suzuki Sm, Leinfelder KF, Katoh Y. How heat treatment and thermal cycling affect wear of composite resin inlays. J Am Dent Assoc, 125(11), 1467-1472, 1994.

상세보기
Shinohara N, Minesaki Y, Mukoyoshi N, Moriyama H, Jimi T. The effect of the cementing material on the strength of the all ceramic crown. Nihon Hotetsu Shika Gakkai Zasshi, 33(2), 416-421, 1989.

상세보기
Thordrup M, Isidor F, Horsted-Bindslev P. Comparison of marginal fit and microleakage of ceramic and composite inlays: an in vitro study. J Dent, 22(3), 147-153, 1994.

상세보기
Touati B, Aidan N. Second generation laboratory composite resins for indirect restorations. J Esthet Restor Dent, 9(3), 108-118, 1997.

상세보기
Wendt JrS. The effect of heat used as a secondary cure upon the physical properties of three composite resins. I. Diametral tensile strength, compressive strength and marginal dimensional stability. Quintessence Int, 18, 265-271, 1987.
Wendt S. Effect of heat on the physical-properties of composite resins. J Dent Res, 1986.
강현숙, 최호영. 와동 복합레진 인레이 충전 후 변연누출에관한 연구. 대한치과보존학회지 17, 191-205, 1992.
조성아, 조영곤, 문주훈. 중합방법에 따른 복합레진 인레이의 물리적 성질에 관한 연구. 구강생물학연구, 20(2), 73-87, 1996.

저자의 다른 논문 :

표제어: PCR

동의어: Packet Collision Rate

용어 설명 출처 목록 (6)

용어 설명: PCR은 세균 특이성이 있는 primer를 이용하여 적은 수의 세균이 있을지라도 쉽게 검출할 수 있는 유용한 방법이며, 이를 이용하여 구강 내 치면세균막이나 타액에서 직접 세균을 검출할 수 있게 되었다[8].

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증