NTIS 바로가기材料 = Journal of the Society of Materials Science, Japan, v.58 no.9, 2009년, pp.773 - 780
松永 久生 (福岡大学) , 村本 諭始 (工学) , 庄村 直哉 (部機械工学) , 遠藤 正浩 (科)
The shear mode propagation and threshold behaviors of small, semi-elliptical fatigue cracks were investigated in the JIS-SUJ2 bearing steel. Fully-reversed torsional loading was combined with a static axial compressive load to obtain crack growth in the longitudinal direction of cylindrical specimen...
10.1299/kikaia.59.283 1) Y. Murakami, “Application of fracture mechanics to tribology problems”, Transactions of the Japan Society of Mechanical Engineers, Series A, Vol.59, pp.283-290 (1993).
0514-5163 OTSUKA AKIO 43 484 55 1994 10.2472/jsms.43.55
0915-1168 MATSUDA KENJI 47 8 636 2002
Beretta, S., Boniardi, M., Carboni, M., Desimone, H.. Mode II fatigue failures at rail butt-welds. Engineering failure analysis, vol.12, no.1, 157-165.
0514-5163 OKOMORI YOSHIHIRO 50 3 249 2001 10.2472/jsms.50.249
0514-5163 FUJII YUKIO 50 10 1108 2001 10.2472/jsms.50.1108
OTSUKA, A., FUJII, Y., MAEDA, K.. A new testing method to obtain mode II fatigue crack growth characteristics of hard materials. Fatigue & fracture of engineering materials & structures, vol.27, no.3, 203-212.
西澤 英雄, 小川 武史. モードII疲労き裂進展特性とき裂駆動力の実験的評価. 材料 = Journal of the Society of Materials Science, Japan, vol.54, no.12, 1295-1300.
0514-5163 MURAKAMI YUKITAKA 51 8 918 2002 10.2472/jsms.51.918
MURAKAMI, Yukitaka, NATSUME, Hiroshi. Stress Singularity at the Corner Point of 3-D Surface Crack under Mode II Loading. JSME international journal. Series A, Solid mechanics and material engineering, vol.45, no.2, 161-169.
10.1007/BF00032701 11) L. P. Pook, “A note on corner point singularities”, International Journal of Fracture, Vol.53, pp.R3-R8 (1992).
Pook, L.P.. Some implications of corner point singularities. Engineering fracture mechanics, vol.48, no.3, 367-378.
Bazant, Z.P., Estenssoro, L.F.. Surface singularity and crack propagation. International journal of solids and structures, vol.15, no.5, 405-426.
10.1115/1.3625127 14) M. K. Kassir and G. C. Sih, “Three-dimensional stress distribution around an elliptical crack under arbitrary loadings”, Journal of Applied Mechanics, Vol.33, pp.601-611 (1966).
MURAKAMI, Y., TAKAHASHI, K., KUSUMOTO, R.. Threshold and growth mechanism of fatigue cracks under mode II and III loadings. Fatigue & fracture of engineering materials & structures, vol.26, no.6, 523-531.
10.1016/j.engfracmech.2007.01.030 16) Y. Murakami, Y. Fukushima, K. Toyama and S. Matsuoka, “Fatigue crack path and threshold in mode II and mode III loadings”, Engineering Fracture Mechanics, Vol.75, pp.306-318 (2008).
戸山 恭平, 福島 良博, 村上 敬宜. 真空中と大気中におけるモードII疲労き裂進展機構とき裂進展下限界値. 材料 = Journal of the Society of Materials Science, Japan, vol.55, no.8, 719-725.
0021-1575 HARADA HISASHI 89 7 789 2003 10.2355/tetsutohagane1955.89.7_789
0021-1575 HARADA HISASHI 91 6 567 2005 10.2355/tetsutohagane1955.91.6_567
0915-1168 HIRAOKA KAZUHIKO 52 12 888 2007
0915-1168 HIRAOKA KAZUHIKO 51 10 744 2006
塚口 友一, 林 浩史, 栗本 英典, 横谷 真一郎, 丸川 雄浄, 田中 敏宏. スラブ連続鋳造用旋回流浸漬ノズルの開発. 鐵と鋼 = Journal of the Iron and Steel Institute of Japan = Tetsu to hagane, vol.95, no.1, 33-42.
23) H. Kinoshita, K. Hiraoka and K. Kobayashi, “The study of microstructural changes during rolling contact fatigue”, Sanyo Technical Report, Vol.7, pp.62-64 (2000).
Selecká, Marcela, Šalak, Andrej. Durability and failure of powder forged rolling bearing rings. Wear: An international journal on the science and technology of friction, lubrication and wear, vol.236, no.1, 47-54.
0915-1168 YOSHIOKA TAKEO 46 9 692 2001
Tschegg, E.K.. Sliding mode crack closure and mode III fatigue crack growth in mild steel. Acta metallurgica, vol.31, no.9, 1323-1330.
28) M. C. Smith and R. A. Smith, “Toward an understanding of mode II fatigue crack growth”, Basic Questions in Fatigue : Volume I, R. P. Wei and R. P. Gangloff, Eds., ASTM STP 924, pp.260-280 (1988).
10.1299/kikaia.63.1627 29) K. Tanaka, Y. Akiniwa and H. Yu, “Near-threshold fatigue crack propagation under mode III torsional loading”, Transactions of the Japan Society of Mechanical Engineers, Series A, Vol.63, pp.1627-1633 (1997).
Campbell, J.P, Ritchie, R.O. Mixed-mode, high-cycle fatigue-crack growth thresholds in Ti–6Al–4V : II. Quantification of crack-tip shielding. Engineering fracture mechanics, vol.67, no.3, 229-249.
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
출판사/학술단체 등이 한시적으로 특별한 프로모션 또는 일정기간 경과 후 접근을 허용하여, 출판사/학술단체 등의 사이트에서 이용 가능한 논문
※ AI-Helper는 부적절한 답변을 할 수 있습니다.