[논문]Weld strength improvement for Al alloy by using laser weaving method

Choi, Kwang-Deok; Ahn, Young-Nam; Kim, Cheolhee

doi:10.2351/1.3499456

Weld strength improvement for Al alloy by using laser weaving method

Journal of laser applications, v.22 no.3, 2010년, pp.116 - 119

Choi, Kwang-Deok (Advanced Welding & Joining Technology Research Team, Korea Institute of Industrial Technology, 7-47 Songdo-Dong, Yeonsu-Gu, Incheon 406-840, Korea) , Ahn, Young-Nam (Advanced Welding & Joining Technology Research Team, Korea Institute of Industrial Technology, 7-47 Songdo-Dong, Yeonsu-Gu, Incheon 406-840, Korea) , Kim, Cheolhee (Advanced Welding & Joining Technology Research Team, Korea Institute of Industrial Technology, 7-47 Songdo-Dong, Yeonsu-Gu, Incheon 406-840, Korea)

Abstract ▼ AI-Helper

Laser welding of aluminum alloys usually produces linear welds that have shear-tensile strength lower than that of the base metal. This is usually due to porosity resulting from an unstable keyhole and cracking which is related to the high crack sensitivity of many of these alloys. In this work laser weaving is used to improve the joint strength of laser welds. In this research, lap welds and bead-on-plate welds were produced on 1 mm thick aluminum alloy sheets using various weaving schemes. When the weaving width was 4 mm, crack propagation was reduced, compared with a weaving width of 2mm. No cracks occurred when the weaving frequency was 5 Hz for weaving widths of 2 and 4 mm. The shear-tensile strengths were measured according to the weaving parameters such as weaving width and frequency. The laser weaving increased the fusion line length, therefore improving the joint strength.

참고문헌 (21)

Kobelco Technol. Rev. 26 55 2005 Wrought aluminum technologies for automobiles
Int. Mater. Rev. 44-6 238 1999 10.1179/095066099101528298 Current issues and problems in laser welding of automotive aluminium alloys

상세보기
Weld. Int. 17-3 173 2003 10.1533/wint.2003.3074 Recent Technological development in welding of aluminium and its alloys

상세보기
Sci. Technol. Weld. Join. 6-3 182 2001 10.1179/136217101101538730 CO2 and Nd-YAG laser beam welding of 5754-O aluminium alloy for automotive applications

상세보기
J. Mater. Process. Technol. 115-1 2 2001 10.1016/S0924-0136(01)00756-7 Light-weight structures produced by laser beam joining for future applications in automobile and aerospace industry

상세보기
Metall. Trans. A 16A-7 1345 1985 Grain structure and solidification cracking in oscillated arc welds of 5052 aluminum alloy
Proc. SPIE 4831 230 2003 10.1117/12.497901 Fan shaped cracking test of aluminum alloys in laser welding
Sci. Technol. Weld. Joining 14-2 161 2009 10.1179/136217108X386554 Characterisation of solidification cracking in pulsed Nd:YAG laser welding of 2024 aluminium alloy

상세보기
Weld. J. 45-6 241s 1966 Preventing weld cracks in high strength aluminium alloys
J. Inst. Met. 74 439 1948 Cracking during the casting and welding of the more common binary aluminium alloys
Weld. J. 31-10 448s 1952 Weld cracking of aluminum alloys
Int. J. KWS 1-1 63 2001 Effect of the Mg content on the solidification cracking susceptibility of the Al-Mg alloy laser welds
Int. J. KWS 2-2 42 2002 Solidification cracking susceptibility of Al-Mg-Si Alloy Laser Welds
Weld. World 50-11/12 46 2006 Influence of the weld metal chemical composition on the solidification cracking susceptibility of AA6056-T4 alloy
Weld. J. 87-1 18s 2008 Effects of Temporal Pulse Shaping on Cracking Susceptibility of 6061-T6 Aluminum Nd:YAG Laser Welds
277 2008
Mater. Sci. Eng., A 519-1-2 167 2009 The relation between liquation and solidification cracks in pulsed laser welding of 2024 aluminium alloy
180 1998
2008
27 2009
Trans. JWRI 11-2 87 1982 A new test specimen for self-restraint solidification crack susceptibility test of electron-beam welding bead

LOADING...

원문 URL 링크

DOI : 10.2351/1.3499456
Laser Institute of America : 저널

*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.

이 논문과 함께 이용한 콘텐츠

[논문] Solidification crack and morphology for laser weave welding of Al 5J32 alloy

저작권 관리 안내

내보내기 메뉴

내보내기 구분

파일저장
인쇄
메일전송

구성항목

기본정보
상세정보

관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관

저장형식

Text(ASCII format)
Excel format
RefWorks Direct Export
RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley

메일정보

받는사람 (필수): @
보내는사람 (선택): @
제목
내용: KISTI 검색결과 이메일 서비스

안내

총 건의 자료가 검색되었습니다.

다운받으실 자료의 인덱스를 입력하세요. (1-10,000)

검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다.

데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요)

다운로드 파일은 UTF-8 형태로 저장됩니다.
파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오.

Text(ASCII format)
Excel format

표제어: PCR

동의어: Packet Collision Rate

용어 설명 출처 목록 (6)

용어 설명: PCR은 세균 특이성이 있는 primer를 이용하여 적은 수의 세균이 있을지라도 쉽게 검출할 수 있는 유용한 방법이며, 이를 이용하여 구강 내 치면세균막이나 타액에서 직접 세균을 검출할 수 있게 되었다[8].

AI-Helper ※ AI-Helper는 을 사용합니다.

AI-Helper

안녕하세요, AI-Helper입니다. 좌측 "선택된 텍스트"에서 텍스트를 선택하여 요약, 번역, 용어설명을 실행하세요.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.

연합인증