NTIS 바로가기Procedia engineering, v.10, 2011년, pp.3220 - 3225
Montoro, S.R. , Shiino, M.Y. , Cruz, T.G.d. , Cioffi, M.O.H. , Woorwald, H.J.C.
A major difficulty to achieve maximum weight savings in the manufacture of composite structural components, is the tendency of these materials have the formation of voids and cracks in the interior and surface components. In aeronautical applications, controlling the volume fraction of fibers, resin...
Composite Science and Technology Costa 61 14 2101 2001 10.1016/S0266-3538(01)00157-9 Almeida SFM. The influence of porosity on the interlaminar shear strength of carbon/epoxy and carbon/bismaleimide fabric laminates
Journal of Composite Materials Jeong 31 3 276 1997 10.1177/002199839703100303 Effects of voids on the mechanical strength and ultrasonic attenuation of laminated composites
Savage 1993 Carbon-carbon composites
Composite Structures Almeida 28 139 1994 10.1016/0263-8223(94)90044-2 Effect of void content on the strength of composite laminates
NonDestructive Testing Stone 137 1975 10.1016/0029-1021(75)90023-7
Giovedi C, Marinucci G, Rouse PR, Claudio ALL. Determinacao das fracoes volumetricas de composite de fibra de carbono e matriz epoxi por diferentes metodologias. In: 16° CBECIMAT, 2004, Porto Alegre.
Marinucci G, Andrade AHP. Microstructural study of polimeric composite cylinders. In: II Materials Research Society Meeting, 2003, Rio de Janeiro.
Polimeros: Ciencia e Tecnologia Costa 11 4 182 2001 10.1590/S0104-14282001000400008 Resistencia ao cisalhamento interlaminar de composites com resina epoxi com diferentes arranjos das fibras na presenca de vazios
Composites Science and Technology Kosek 69 9 1465 2009 10.1016/j.compscitech.2008.05.010 Visualization of voids in actual C/C woven composite structure
Transactions of Nonferrous Metals Society of China Zhu 19 470 2009 10.1016/S1003-6326(10)60091-X
Composite Structures Liu 73 3 303 2006 10.1016/j.compstruct.2005.02.001 Effects of cure cycles on void content and mechanical properties of composite laminates
ASTM D 3171, Standard Test Methods for Constituent Content of Composite Materials, p. 1-10, 2009.
ASTM C830, Standard Test Methods for Apparent Porosity, Liquid Absorption, Apparent Specific Gravity, and Bulk Density of Refractory Shapes by Vacuum Pressure, p. 1-5, 2006.
ASTM D790-10, Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials, p. 1-11, 2010.
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
저자가 APC(Article Processing Charge)를 지불한 논문에 한하여 자유로운 이용이 가능한, hybrid 저널에 출판된 논문
※ AI-Helper는 부적절한 답변을 할 수 있습니다.