[논문]Annealing induced structural evolution and electrochromic properties of nanostructured tungsten oxide films

Wu, C.L.; Lin, C.K.; Wang, C.K.; Wang, S.C.; Huang, J.L.

doi:10.1016/j.tsf.2013.06.022

Annealing induced structural evolution and electrochromic properties of nanostructured tungsten oxide films

Thin solid films, v.549, 2013년, pp.258 - 262

Wu, C.L. , Lin, C.K. , Wang, C.K. , Wang, S.C. , Huang, J.L.

Abstract ▼ AI-Helper

The effect of microstructure on the optical and electrochemical properties of nanostructured tungsten oxide films was evaluated as a function of annealing temperature. The films using block copolymer as the template were prepared from peroxotungstic acid (PTA) by spin-coating onto the substrate and post-annealed at 250-400oC to form tungsten oxide films with nanostructure. The microstructure of the films was measured by X-ray diffraction and surface electron microscopy. The films annealed at temperatures below 300oC are characterized by amorphous or nanocrystalline structures with a pore size of less than 10nm. The evaluated annealing temperature caused a triclinic crystalline structure and microcracks. Cyclic voltammetry measurements were performed in a LiClO4-propylene carbonate electrolyte. The results showed that the ion inserted capacity were maximized for films annealed at 300oC and decreased with the increasing of annealing temperature. The electrochromic properties of the nanostructured tungsten oxide films were evaluated simultaneously by potentiostat and UV-vis spectroscopy. The films annealed at 300oC exhibit high transmission modulation (@?T~40%) at λ=633nm and good kinetic properties. As a result, the correlation between the microstructure and kinetic properties was established, and the electrochromic properties have been demonstrated.

주제어

참고문헌 (24)

Chem. Mater. Pan 18 847 2006 10.1021/cm0522782

상세보기
Monk 2007 Electrochromism and Electrochromic Devices
Granqvist 1995 Handbook of Inorganic Electrochromic Materials
Chem. Mater. Blackman 17 1583 2005 10.1021/cm0403816

상세보기
Appl. Phys. Lett. Faughnan 31 834 1977 10.1063/1.89566

상세보기
Thin Solid Films Lin 520 1375 2011 10.1016/j.tsf.2011.08.074

상세보기
Nanotechnology Deepa 17 2625 2006 10.1088/0957-4484/17/10/030

상세보기
Sol. Energy Mater. Sol. Cells Deepa 90 2665 2006 10.1016/j.solmat.2006.02.032

상세보기
Acta Mater. Deepa 55 6095 2007 10.1016/j.actamat.2007.07.056

상세보기
J. Mater. Chem. Qi 14 3540 2004 10.1039/b411244j

상세보기
J. Mater. Chem. Cheng 11 92 2001 10.1039/b003192p

상세보기
J. Mater. Chem. Lin 22 16817 2012 10.1039/c2jm32742b

상세보기
Microporous Mesoporous Mater. Ko 145 141 2011 10.1016/j.micromeso.2011.05.008

상세보기
Chem. Mater. Alberius 14 3284 2002 10.1021/cm011209u

상세보기
Electrochim. Acta Deepa 51 1974 2006 10.1016/j.electacta.2005.06.027

상세보기
Surf. Coat. Technol. Wu 2012
Microporous Mesoporous Mater. Taguchi 21 387 1998 10.1016/S1387-1811(98)00127-9

상세보기
Electrochim. Acta Deepa 50 3545 2005 10.1016/j.electacta.2005.01.008

상세보기
Solid State Ionics Srivastava 176 1161 2005 10.1016/j.ssi.2004.10.006

상세보기
Curr. Appl. Phys. Vijaylakshmi 3 171 2003 10.1016/S1567-1739(02)00196-7

상세보기
Sol. Energy Mater. Sol. Cells Wang 58 411 1999 10.1016/S0927-0248(99)00017-3

상세보기
J. Sol-gel Sci. Tech. Wang 54 19 2010 10.1007/s10971-010-2152-6

상세보기
J. Mater. Chem. C Kattouf 1 151 2013 10.1039/C2TC00291D

상세보기
Thin Solid Films Barbosa 516 1480 2008 10.1016/j.tsf.2007.03.154

상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Annealing induced structural evolution and electrochromic properties of nanostructured tungsten oxide films

Abstract ▼ AI-Helper

주제어

참고문헌 (24)

이 논문을 인용한 문헌

관련 콘텐츠

원문 URL 링크

이 논문과 함께 이용한 콘텐츠

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트