NTIS 바로가기Construction & building materials, v.50, 2014년, pp.169 - 176
Jang, J.G. , Lee, N.K. , Lee, H.K.
This paper presents results of an experimental study carried out to investigate fresh and hardened properties of alkali-activated fly ash/slag pastes with superplasticizers. The binders were prepared by dry mixing of slag and fly ash with 5 slag-to-binder ratios, 0, 0.3, 0.5, 0.7, and 1. An alkali a...
Cem Concr Res Gartner 34 9 1489 2004 10.1016/j.cemconres.2004.01.021 Industrially interesting approaches to “low-CO2” cements
J Mater Sci Duxson 42 9 2917 2007 10.1007/s10853-006-0637-z Geopolymer technology: the current state of the art
Davidovits J, Buzzi L, Rocher P, Gimeno D, Marini C, Tocco S, Geopolymeric cement based on low cost geologic materials. Results from the european research project geocistem. In: Proceedings of the 2nd international conference on geopolymer, June 30-July 2, France, Saint Quentin, 1999, p. 83-96.
Cem Concr Comp Chindaprasirt 29 3 224 2007 10.1016/j.cemconcomp.2006.11.002 Workability and strength of coarse high calcium fly ash geopolymer
Cem Concr Comp Guo 32 2 142 2010 10.1016/j.cemconcomp.2009.11.003 Compressive strength and microstructural characteristics of class C fly ash geopolymer
Cem Concr Res Lee 32 4 577 2002 10.1016/S0008-8846(01)00724-4 The effect of ionic contaminants on the early-age properties of alkali-activated fly ash-based cements
Fire Mater Lyon 21 2 67 1997 10.1002/(SICI)1099-1018(199703)21:2<67::AID-FAM596>3.0.CO;2-N Fire-resistant aluminosilicate composites
Cem Concr Res Garcia-Lodeiro 37 2 175 2007 10.1016/j.cemconres.2006.11.002 Alkali-aggregate reaction in activated fly ash systems
Lee NK, Jang JG, Lee HK, Effect of blast furnace slag on drying shrinkage of fly ash-based paste and mortar activated with sodium silicate, In: The 5th international conference of Asian concrete federation, Pattaya, Thailand, October 24-26, 2012.
Ind Eng Chem Res Duxson 45 23 7781 2006 10.1021/ie060187o Thermal conductivity of metakaolin geopolymers used as a first approximation for determining gel interconnectivity
ACI Mater J Gifford 93 3 242 1996 Freeze thaw durability of activated blast furnace slag cement concrete
Ceram-Silikaty Skvara 49 3 195 2005 Geopolymer materials based on fly ash
Cem Concr Comp Sata 34 5 700 2012 10.1016/j.cemconcomp.2012.01.010 Resistance of lignite bottom ash geopolymer mortar to sulfate and sulfuric acid attack
Cem Concr Res Shi 41 7 750 2011 10.1016/j.cemconres.2011.03.016 New cements for the 21st century: the pursuit of an alternative to Portland cement
Cem Concr Res Puertas 30 10 1625 2000 10.1016/S0008-8846(00)00298-2 Alkali-activated fly ash/slag cement strength behaviour and hydration products
Constr Build Mater Lee 47 1201 2013 10.1016/j.conbuildmat.2013.05.107 Setting and mechanical properties of alkali activated fly ash/slag concrete manufactured at room temperature
Cem Concr Res Brough 30 9 1375 2000 10.1016/S0008-8846(00)00356-2 Sodium silicate-based alkali-activated slag mortars, Part II. The retarding effect of additions of sodium chloride or malic acid
Cem Concr Res Douglas 20 5 746 1990 10.1016/0008-8846(90)90008-L A preliminary study on the alkali activation of ground granulated blast-furnace slag
Cem Concr Res Palacios 35 7 1358 2005 10.1016/j.cemconres.2004.10.014 Effect of superplasticizer and shrinkage-reducing admixtures on alkali-activated slag pastes and mortars
Cement J Co. Ltd. Ando 22 1995 New generation concrete
Cem Concr Res Yamada 30 2 197 2000 10.1016/S0008-8846(99)00230-6 Effects of the chemical structure on the properties of polycarboxylate-type superplasticizer
Cem Concr Res Yip 35 9 1688 2005 10.1016/j.cemconres.2004.10.042 The coexistence of geopolymeric gel and calcium silicate hydrate at the early stage of alkaline activation
Thermochim Acta Ravikumar 546 32 2012 10.1016/j.tca.2012.07.010 Reaction kinetics in sodium silicate powder and liquid activated slag binders evaluated using isothermal calorimetry
Cem Concr Comp Ravikumar 34 7 809 2012 10.1016/j.cemconcomp.2012.03.006 Effects of activator characteristics on the reaction product formation in slag binders activated using alkali silicate powder and NaOH
American society for testing and materials, ASTM C191-08: Standard test methods for time of setting of hydraulic cement by Vicat needle, ASTM int, 2008.
American Society for Testing and Materials, ASTM C1437-07: Standard test method for flow of hydraulic cement mortar, ASTM Int, 2013.
American Society for Testing and Materials, ASTM C109: Standard test method for compressive strength of hydraulic cement mortars, ASTM Int, 2013
American Society for Testing and Materials, ASTM C150: Standard specification for Portland cement, ASTM Int, 2012.
Resour Conserv Recy Zhao 52 2 303 2007 10.1016/j.resconrec.2007.04.002 Activated fly ash/slag blended cement
*원문 PDF 파일 및 링크정보가 존재하지 않을 경우 KISTI DDS 시스템에서 제공하는 원문복사서비스를 사용할 수 있습니다.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.