[논문]Morphology-controlled synthesis, characterization and microwave absorption properties of nanostructured 3D CeO2

Wu, G.; Cheng, Y.; Xiang, F.; Jia, Z.; Xie, Q.; Wu, G.; Wu, H.

doi:10.1016/j.mssp.2015.06.077

Morphology-controlled synthesis, characterization and microwave absorption properties of nanostructured 3D CeO2

Materials science in semiconductor processing, v.41, 2016년, pp.6 - 11

Wu, G. , Cheng, Y. , Xiang, F. , Jia, Z. , Xie, Q. , Wu, G. , Wu, H.

Abstract ▼ AI-Helper

Nanostructured 3D CeO2 have been synthesized by using PEG 2000 assisted simple hydrothermal technique. The impact of this novel approach on the structure, morphology, spectroscopy, complex permittivity and permeability was discussed. CeO2 was studied by employing X-ray diffraction (XRD), Raman spectra, field emission scanning electron microscopy (FE-SEM), thermogravimetric analysis (TG) and vector network analyzer. It can be seen that the microspheres of 1-3μm in diameter were prepared at 600oC with a mole ratio of 2:1, while the decreasing concentration of PEG-2000 resulted in the appearance of dim side-shape geometry. Obviously, the morphology of the synthesized CeO2 gradually changed from sphere with relatively smooth to irregular side-shape annealed at 600oC with the increase of mole ratio for reactants. The electromagnetic (EM) wave absorption properties of the synthesized CeO2 were investigated over the range from 2 to 16GHz, and minimum reflection loss (RL) with -19.3dB was observed at 15.8GHz with the thickness of 2.0mm. This phenomenon may be attributed to both intrinsic characteristic of CeO2 and preparation with the function of PEG-2000.

주제어

참고문헌 (51)

J. Mater. Chem. A Wang 3 2734 2015 10.1039/C4TA06053A

상세보기
Adv. Mater. Wen 26 3484 2014 10.1002/adma.201400108

상세보기
Adv. Opt. Mater. Yang 2 214 2014 10.1002/adom.201300439

상세보기
Carbon Wen 65 124 2013 10.1016/j.carbon.2013.07.110

상세보기
ACS Appl. Mater. Interfaces Cao 4 6949 2012 10.1021/am3021069

상세보기
Phys. Chem. Chem. Phys. Wang 17 3802 2015 10.1039/C4CP04228J

상세보기
Chem. Eur. J. Liu 19 6746 2013 10.1002/chem.201203557

상세보기
Polym. Adv. Technol. Phang 20 550 2009 10.1002/pat.1381

상세보기
J. Magn. Magn. Mater. Dadfar 324 4204 2012 10.1016/j.jmmm.2012.07.046

상세보기
J. Am. Ceram. Soc. Kong 95 3158 2012 10.1111/j.1551-2916.2012.05278.x

상세보기
J. Appl. Phys. Zhuo 104 094101 2008 10.1063/1.2973198

상세보기
J. Phys. Chem. C Li 114 10088 2010 10.1021/jp100341h

상세보기
Mater. Lett. Wu 92 139 2013 10.1016/j.matlet.2012.10.093

상세보기
Powder Technol. Zhao 270 20 2015 10.1016/j.powtec.2014.10.001

상세보기
Solid State Commun. Liu 149 64 2009 10.1016/j.ssc.2008.10.015

상세보기
Mater. Chem. Phys. Zhang 130 615 2011 10.1016/j.matchemphys.2011.07.033

상세보기
J. Eur. Ceram. Soc. Loghman-Estarki 35 693 2015 10.1016/j.jeurceramsoc.2014.08.029

상세보기
Ceram. Int. Davar 39 2933 2013 10.1016/j.ceramint.2012.09.067

상세보기
Curr. Nanosci. Loghman-Estarki 8 767 2012 10.2174/157341312802884364

상세보기
CrystEngComm Loghman-Estarki 15 5898 2013 10.1039/c3ce40288f

상세보기
Appl. Catal. B - Environ. Liotta 66 217 2006 10.1016/j.apcatb.2006.03.018

상세보기
Catal. Sci. Technol. Wu 5 1888 2015 10.1039/C4CY01158A
CrystEngComm Wei 13 2418 2011 10.1039/c0ce00635a

상세보기
Sens. Actuators B Michel 197 177 2014 10.1016/j.snb.2014.02.090

상세보기
Ceram. Int. Kashyap 40 11869 2014 10.1016/j.ceramint.2014.04.021

상세보기
Appl. Surf. Sci. Wu 258 10047 2012 10.1016/j.apsusc.2012.06.072

상세보기
Mater. Lett. Meng 100 86 2013 10.1016/j.matlet.2013.03.029

상세보기
Mater. Chem. Phys. Singhal 132 534 2012 10.1016/j.matchemphys.2011.11.066

상세보기
Appl. Phys. Lett. Ge 93 062505 2008 10.1063/1.2972118

상세보기
Mater. Res. Bull. Wang 48 3492 2013 10.1016/j.materresbull.2013.05.036

상세보기
Appl. Phys. Lett. Joo 65 2278 1994 10.1063/1.112717

상세보기
Synth. Met. Lee 102 1346 1999 10.1016/S0379-6779(98)00234-3

상세보기
J. Mater. Chem. Xia 11 2925 2001 10.1039/b105548h

상세보기
Microporous Mesoporous Mater. Rao 169 81 2013 10.1016/j.micromeso.2012.10.021

상세보기
Appl. Catal. B - Environ. Slavinskaya 166-167 91 2015 10.1016/j.apcatb.2014.11.015

상세보기
Mater. Lett. Hadi 61 93 2007 10.1016/j.matlet.2006.04.013

상세보기
Mater. Charact. Supakanapitak 67 83 2012 10.1016/j.matchar.2012.02.018

상세보기
Mater. Res. Bull. Purohita 36 2711 2001 10.1016/S0025-5408(01)00762-0

상세보기
J. Alloy. Compd. Mahata 391 129 2005 10.1016/j.jallcom.2004.07.085

상세보기
Mater. Lett. Bo 133 216 2014 10.1016/j.matlet.2014.07.052

상세보기
Inorg. Chem. Zhang 46 2446 2007 10.1021/ic061697d

상세보기
Phys. Rev. B Weber 48 178 1993 10.1103/PhysRevB.48.178

상세보기
Mater. Chem. Phys. Wang 68 246 2001 10.1016/S0254-0584(00)00357-6

상세보기
Thin Solid Films Kanakaraju 305 191 1997 10.1016/S0040-6090(97)00081-3

상세보기
J. Chem. Soc. Dalton Trans. Burroughs 17 1686 1976 10.1039/dt9760001686

상세보기
Surf. Sci. Mullins 409 307 1998 10.1016/S0039-6028(98)00257-X

상세보기
Chem. Mater. Abi-aad 5 793 1993 10.1021/cm00030a013

상세보기
Chem. Mater. Kruk 13 3169 2001 10.1021/cm0101069

상세보기
Adv. Colloid Interface Sci. Sing 76-77 3 1998 10.1016/S0001-8686(98)00038-4

상세보기
Pal 3 10837 2013
Appl. Phys. Lett. Wang 102 223113 2013 10.1063/1.4809675

상세보기

내보내기 구분	파일저장 인쇄 메일전송
구성항목	기본정보 상세정보 관리번호, 논문명, 저널/프로시딩명, 저자 , 발행년, 권, 호, 시작페이지, 끝페이지, 발행기관 관리번호, 논문명, 대등논문명, 저자 , 저널/프로시딩명, 발행기관, 발행년, 발행언어, 권, 호, 시작페이지, 끝페이지, ISBN, ISSN, 주제분야, 키워드, 초록(한글), 초록(영문), 저자(소속기관)
저장형식	Text(ASCII format) Excel format RefWorks Direct Export RIS format (for Reference Manager, ProCite, EndNote), Scholar's Aids, Mendeley
메일정보	받는사람 (필수) @ 보내는사람 (선택) @ 제목 내용 KISTI 검색결과 이메일 서비스
안내	총 건의 자료가 검색되었습니다. 다운받으실 자료의 인덱스를 입력하세요. (1-10,000) 검색결과의 순서대로 최대 10,000건 까지 다운로드가 가능합니다. 데이타가 많을 경우 속도가 느려질 수 있습니다.(최대 2~3분 소요) 다운로드 파일은 UTF-8 형태로 저장됩니다. 파일의 내용이 제대로 보이지 않을실 때는 웹브라우저 상단의 보기 -> 인코딩 -> 자동선택 여부를 확인하십시오. ~ Text(ASCII format) Excel format

연합인증

Morphology-controlled synthesis, characterization and microwave absorption properties of nanostructured 3D CeO2

Abstract ▼ AI-Helper

주제어

참고문헌 (51)

이 논문을 인용한 문헌

관련 콘텐츠

원문 URL 링크

AI-Helper ※ AI-Helper는 오픈소스 모델을 사용합니다.

선택된 텍스트