NTIS 바로가기Materials, v.11 no.6, 2018년, pp.883 -
Liu, Zhaoyang , Yu, Jingkun , Yang, Xin , Jin, Endong , Yuan, Lei
Various carbon contents in the MgO-C refractory were studied with respect to the oxidation resistance and the wetting behavior with slag. The bulk density, apparent porosity, cold crushing strength, oxidation rate, and mass loss rate of the fired MgO-C refractories with various carbon contents were ...
1. Zhang S.W. Lee W.E. Influence of additives on corrosion resistance and corroded microstructures of MgO-C refractories J. Eur. Ceram. Soc. 2001 21 2393 2405 10.1016/S0955-2219(01)00208-4
2. Li Z. Mukai K. Tao Z. Reactions between MgO-C refractory, molten slag and metal ISIJ Int. 2000 40 101 105 10.2355/isijinternational.40.Suppl_S101
3. Zhu T. Li Y. Sang S. Xie Z. Mechanical behavior and thermal shock resistance of MgO-C refractories: Influence of graphite content Ceram. Int. 2017 43 7177 7183 10.1016/j.ceramint.2017.03.004
4. Liu Q.C. Chen D.F. Xu Y. Newkirk J.W. Corrosion resistance of MgO-C refractory to smelting reduction slag containing titania Brit. Corros. J. 2002 37 231 234 10.1179/000705902225004392
5. Han B. Ke C. Wei Y. Yan W. Wang C. Chen F. Li N. Degradation of MgO-C refractories corroded by SiO 2 -Fe 2 O 3 -V 2 O 5 -TiO 2 -MnO-MgO slag Ceram. Int. 2015 41 10966 10973 10.1016/j.ceramint.2015.05.040
6. Mukai K. Li Z. Tao Z. Bubble generation in MgO-C crucible charged with slag and metal in relation to local corrosion High Temp. Mater. Process. 2011 20 255 262 10.1515/HTMP.2001.20.3-4.255
7. Jansson S. Brabie V. Jonsson P. Corrosion mechanism of commercial MgO-C refractories in contact with different gas atmospheres ISIJ Int. 2008 48 760 767 10.2355/isijinternational.48.760
8. Jansson S. Brabie V. Bohlin L. Corrosion mechanism and kinetic behaviour of refractory materials in contact with CaO-Al 2 O 3 -MgO-SiO 2 slags Scand. J. Metall. 2004 34 283 292 10.1111/j.1600-0692.2005.00748.x
9. Zhu T. Li Y. Sang S. Xie Z. Fracture behavior of low carbon MgO-C refractories using the wedge splitting test J. Eur. Ceram. Soc. 2017 37 1789 1797 10.1016/j.jeurceramsoc.2016.11.013
10. Sadrnezhaad S.K. Mahshid S. Hashemi B. Nemati Z.A. Oxidation mechanism of C in MgO-C refractory bricks J. Am. Ceram. Soc. 2006 89 1308 1316 10.1111/j.1551-2916.2005.00863.x
11. Li X. Rigaud M. Anisotropy of the properties of magnesia-graphite refractories: linear thermal change and carbon oxidation resistance Can. Ceram. Q. 1993 62 197 205
12. Pilli V. Sarkar R. Nanocarbon containing Al 2 O 3 -C continuous casting refractories: effect of graphite content J. Alloys Compd. 2018 735 1730 1736 10.1016/j.jallcom.2017.11.324
13. Li X. Rigaud M. Palco S. Oxidation kinetics of graphite phase in magnesia-carbon refractories J. Am. Ceram. Soc. 1995 78 965 971 10.1111/j.1151-2916.1995.tb08423.x
14. Faghihi-Sani M.A. Yamaguchi A. Oxidation kinetics of MgO-C refractory bricks Ceram. Int. 2002 28 835 839 10.1016/S0272-8842(02)00049-4
15. Sadrnezhaad S.K. Nemati Z.A. Mahshid S. Hosseini S. Hashemi B. Effect of Al antioxidant on the rate of oxidation of carbon in MgO-C refractory J. Am. Ceram. Soc. 2007 90 509 515 10.1111/j.1551-2916.2006.01391.x
16. Hashemi B. Nemati Z.A. Faghihi M.A. Effects of resin and graphite content on density and oxidation behavior of MgO-C refractory bricks Ceram. Int. 2006 32 313 319 10.1016/j.ceramint.2005.03.008
17. Yoon T. Lee K. Lee B. Chung Y. Wetting, spreading and penetration phenomena of slags on MgAl 2 O 4 spinel refractories ISIJ Int. 2017 57 1327 1333 10.2355/isijinternational.ISIJINT-2016-578
18. Kim S. Lee K. Chung Y. Dissolutive wetting and spreading phenomena between Al 2 O 3 substrate and CaO-Al 2 O 3 liquid slags Metall. Mater. Trans. B 2016 47 1209 1216 10.1007/s11663-016-0587-z
19. Hemberger Y. Berthold C. Nickel K.G. Wetting and corrosion of yttria stabilized zirconia by molten slags J. Eur. Ceram. Soc. 2012 32 2859 2866 10.1016/j.jeurceramsoc.2011.12.005
20. Heo S.H. Lee K. Chung Y. Reactive wetting phenomena of MgO-C refractories in contact with CaO-SiO 2 slag Trans. Nonferrous Met. Soc. China 2012 22 870 875 10.1016/S1003-6326(12)61818-4
21. Shen P. Zhang L.F. Wen Y. Wang Y. Wettability and penetration phenomenon between LF refining slag and MgO-C substrate Iron Steel 2016 51 31 40 (in Chinese)
22. Yuan Z. Wu Y. Zhao H. Matsuura H. Tsukihashi F. Wettability between molten slag and MgO-C refractories for the slag splashing process ISIJ Int. 2013 53 598 602 10.2355/isijinternational.53.598
23. Mukai K. Wetting and marangoni effect in iron and steelmaking processes ISIJ Int. 1992 32 19 25 10.2355/isijinternational.32.19
24. Mills K.C. Hondros E.D. Li Z. Interfacial phenomena in high temperature processes J. Mater. Sci. 2005 40 2403 2409 10.1007/s10853-005-1966-z
25. Li X. Zhu B. Wang T. Effect of electromagnetic field on slag corrosion resistance of low carbon MgO-C refractories Ceram. Int. 2012 38 2105 2109 10.1016/j.ceramint.2011.10.049
26. Leonard R.J. Herron R.H. Significance of oxidation-reduction reactions within BOF refractories J. Am. Ceram. Soc. 1972 55 1 6 10.1111/j.1151-2916.1971.tb12392.x-i1
27. Ghosh N.K. Ghosh D.N. Jagannathan K.P. Oxidation mechanism of MgO-C in air at various temperatures Brit. Ceram. Trans. 2000 99 124 128 10.1179/096797800680839
28. Tsypkin G.G. Calore C. Role of capillary forces in vapour extraction from low-permeability, water-saturated geothermal reservoirs Geothermics 2003 32 219 237 10.1016/S0375-6505(03)00018-X
※ AI-Helper는 부적절한 답변을 할 수 있습니다.