Aiming at improving the performance of 22 mm thick X80M hot rolled steel strip DWTT performance, simulated tests and industrial trials were carried out on a 550 mm test mill and a 2250 mm hot tandem mill. The effects of different starting temperature and the end temperature of finish rolling, coolin...
Aiming at improving the performance of 22 mm thick X80M hot rolled steel strip DWTT performance, simulated tests and industrial trials were carried out on a 550 mm test mill and a 2250 mm hot tandem mill. The effects of different starting temperature and the end temperature of finish rolling, cooling rate, coiling temperature on the microstructure and DWTT properties of the test steel were studied. The effects of austenite grain size on DWTT properties were studied by comparing the rough rolling reduction rate and the accumulative deformation rate in the non-recrystallized zone. The results show that uniform and fine original austenite grains can obtain uniform, and fine acicular ferrite lath bundles. The microstructure of acicular ferrite, granular bainite and a large number of fine M/A islands dispersed on ferrite matrix with high density dislocations has better DWTT performance. Meanwhile, the average effective grain size of X80M pipeline steel can be refined to obtain more grain boundary area per unit volume. Large angle grain boundary is beneficial to prevent crack propagation. Improving grain size of X80M pipeline steel strip is an effective measure to improve fracture toughness. Under this chemical composition, the final pass reduction ratio in roughing mill of X80M pipeline steel is ≥26%, the thickness of intermediate slab is 68 mm,the starting temperature of finish rolling is 900 °C, the end temperature of finish rolling is 810 °C, the cooling rate is 25 °C/s, the coiling temperature is below 400 °C, and DWTT toughness fracture ratio can reach more than 85%, which can meet the application requirements of pipeline steel for the extreme conditions of −15 °C in the west-east gas pipeline.
Aiming at improving the performance of 22 mm thick X80M hot rolled steel strip DWTT performance, simulated tests and industrial trials were carried out on a 550 mm test mill and a 2250 mm hot tandem mill. The effects of different starting temperature and the end temperature of finish rolling, cooling rate, coiling temperature on the microstructure and DWTT properties of the test steel were studied. The effects of austenite grain size on DWTT properties were studied by comparing the rough rolling reduction rate and the accumulative deformation rate in the non-recrystallized zone. The results show that uniform and fine original austenite grains can obtain uniform, and fine acicular ferrite lath bundles. The microstructure of acicular ferrite, granular bainite and a large number of fine M/A islands dispersed on ferrite matrix with high density dislocations has better DWTT performance. Meanwhile, the average effective grain size of X80M pipeline steel can be refined to obtain more grain boundary area per unit volume. Large angle grain boundary is beneficial to prevent crack propagation. Improving grain size of X80M pipeline steel strip is an effective measure to improve fracture toughness. Under this chemical composition, the final pass reduction ratio in roughing mill of X80M pipeline steel is ≥26%, the thickness of intermediate slab is 68 mm,the starting temperature of finish rolling is 900 °C, the end temperature of finish rolling is 810 °C, the cooling rate is 25 °C/s, the coiling temperature is below 400 °C, and DWTT toughness fracture ratio can reach more than 85%, which can meet the application requirements of pipeline steel for the extreme conditions of −15 °C in the west-east gas pipeline.
참고문헌 (25)
Baosteel Techn. Res. Zhang 8 2 46 2014
World Iron Steel Li 9 56 2009
China Metall. Xu 26 1 2016
Iron Steel Nie 44 76 2009
J. Iron and Steel Res. Zhou 21 33 2009
J. Northeastern Univ. (Natural Science) Yi 29 213 2008
Heat Treat. Met. Wang 39 94 2014
J. Mech. Engi. Yu 47 44 2011 10.3901/JME.2011.24.044
Hot Work. Technol. Zhao 42 31 2013
Welded Pipe Tube Yang 33 74 2010
Heat Treat. Met. Jia 41 197 2016
Acta Metall. Sinica Zhou 38 283 2002
Mater. Sci. Technol. Zhao 09 356 2001
J. Univ. Sci. Technol. Liu 32 444 2010
J. Univ. Sci. Technol. Ren 29 798 2007
Acta Metall. Sinica Deng 46 533 2010 10.3724/SP.J.1037.2009.00461
※ AI-Helper는 부적절한 답변을 할 수 있습니다.