Change of dielectric loss of use in high relative permitivity capacitor BaTiO$_3$ ceramic depends on Mn doping have been investigated. The powders used in this study were commercial BaTiO$_3$, TiO$_2$and, MnCO$_3$. Sample was fabricated by conventional cer...

Change of dielectric loss of use in high relative permitivity capacitor BaTiO$_3$ ceramic depends on Mn doping have been investigated. The powders used in this study were commercial BaTiO$_3$, TiO$_2$and, MnCO$_3$. Sample was fabricated by conventional ceramic process. The quantity of Mn was changed gradually from 0.lmol% to 10mo1%. The sintering densities were reduced with increasing amount of MnCO$_3$. This result is because of increase of low density second phase BaMnO$_3$. When the samples were doped by over 0.2mol% of MnCO$_3$, average grain sizes were enlarge to several tens ${\mu}{\textrm}{m}$. The dielectric losses were reduced by Mn doping to lmol% but, increased from lmol% to 10mo1% gradually.