Commerical purity aluminium , copper and STS 304 stainless steel sheets are welded by ultrasonic welding. The microstructures, x-ray diffraction profiles of planes , pole figures of the surface of original metal sheets are compared with those of the weld interface. The microstructures show disturban...
Commerical purity aluminium , copper and STS 304 stainless steel sheets are welded by ultrasonic welding. The microstructures, x-ray diffraction profiles of planes , pole figures of the surface of original metal sheets are compared with those of the weld interface. The microstructures show disturbance and dark areas in the weld interface and grain refinement in the vicinity of the interface. The x-ray diffraction intensity of each plane in weld interface decreased in all metal sheets with exception of 9200) in steel sheet. The microstructure and x-ray diffraction intensity is affected by the mixture of deformation, heating and vibratin duringthe ultrasonic welding. Therefore, after the ultrasonic welding, the positions of the peak intensity in the pole figures are changed, the value of the maximum pole intensity is decreased in Al, is increased in copper and stainless steel. Very strong {100} texture, strong {100} ,{123} textures in original Al surface are transformed into weak, {100}, {110} and {112} components in weld surface, weak (110) fiber is slightly changed to (110) fiber in copper, (100)and ${\gamma}$ fiber components are transformed into strong ${\gamma}$ fiber component in stainless steel.
Commerical purity aluminium , copper and STS 304 stainless steel sheets are welded by ultrasonic welding. The microstructures, x-ray diffraction profiles of planes , pole figures of the surface of original metal sheets are compared with those of the weld interface. The microstructures show disturbance and dark areas in the weld interface and grain refinement in the vicinity of the interface. The x-ray diffraction intensity of each plane in weld interface decreased in all metal sheets with exception of 9200) in steel sheet. The microstructure and x-ray diffraction intensity is affected by the mixture of deformation, heating and vibratin duringthe ultrasonic welding. Therefore, after the ultrasonic welding, the positions of the peak intensity in the pole figures are changed, the value of the maximum pole intensity is decreased in Al, is increased in copper and stainless steel. Very strong {100} texture, strong {100} ,{123} textures in original Al surface are transformed into weak, {100}, {110} and {112} components in weld surface, weak (110) fiber is slightly changed to (110) fiber in copper, (100)and ${\gamma}$ fiber components are transformed into strong ${\gamma}$ fiber component in stainless steel.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.