The Purpose of this study is to evaluate the strength characteristics of polyurethane(PUR) mortar cured under low temperature condition. PUR mortars are prepared with various catalyst content, methylene chloride(MC) content as a viscosity reducing agent, and curing age at low temperature condition o...

The Purpose of this study is to evaluate the strength characteristics of polyurethane(PUR) mortar cured under low temperature condition. PUR mortars are prepared with various catalyst content, methylene chloride(MC) content as a viscosity reducing agent, and curing age at low temperature condition of $0^{\circ}C$, -5$^{\circ}C$ and -1$0^{\circ}C$, tested for working life, compressive and flexural strengths. From the test results, the catalyst and MC contents affect the degree of hardening and blowing of PUR mortar. Strengths increase with an increasing catalyst content at low temperature. Flexural and compressive strength of PUR mortar are about 177kgf/$\textrm{cm}^2$ and 490kgf/$\textrm{cm}^2$ respectively at curing temperature of -1$0^{\circ}C$ with catalyst content of 0.4%. Therefore, it is apparent that this PUR mortars have a sufficient strengths for repair of concrete structures.