In the sintering of YIG, abnormal grain growth phenomena was observed. This abnormal grain growth is related to the sintering temperature in this experiment. In the sintering below 145$0^{\circ}C$., the sintered body showed narrow size distribution. However, in the sintering at 145

In the sintering of YIG, abnormal grain growth phenomena was observed. This abnormal grain growth is related to the sintering temperature in this experiment. In the sintering below 145$0^{\circ}C$., the sintered body showed narrow size distribution. However, in the sintering at 145$0^{\circ}C$, a few grains grew rapidly with respect to other grains, and bimodal size distribution was appeared. Liquid phase was not observed far from the abnormally grown large grains, but only near the large grains. This means that the abnormal grain growth was caused by the nonuniform distribution of liquid phase which promote the grains growth. This nonuniform distribution of liquid phase was thought to be due to the nonuniform mixing of the starting materials. This abnormal grain growth was suppressed by enhance the compositional uniformity by multiple calcination.