To investigate the humidity effect on tribological behaviors of Si-DLC/DLC multi-layers, the samples were prepared using a system consisted of an ion-gun for deposition DLC films and a balanced magnetron sputter for introducing silicon atoms to Si-DLC films. The Si-DLC/DLC multi-layers were composed...

To investigate the humidity effect on tribological behaviors of Si-DLC/DLC multi-layers, the samples were prepared using a system consisted of an ion-gun for deposition DLC films and a balanced magnetron sputter for introducing silicon atoms to Si-DLC films. The Si-DLC/DLC multi-layers were composed of pure DLC films and Si-incorporated DLC films alternatively and had different bilayer numbers. Hardness and residual stress were drastically decreased through the formation of Si-DLC/DLC multi-layers compared to those of the pure and Si-incorporated DLC films. Wear results obtained under the various humidity conditions (<10%, $40{\sim}50%$, and >85%) showed that the pure DLC film was largely depended on the humidity while the Si-DLC and the Si-DLC/DLC multi-layers were little affected by the environmental humidity. Although friction coefficients of all samples were increased with the relative humidity, the multi-layer films showed relatively lower friction coefficients that those of the single films.