This study aimed to examine the cause of latent hydraulic property manifestation of ground granulated blast-furnace slag(GGBFS) using different alkali activators in pH, type and quantity. According to the experimental result, the higher pH value accelerated lastly latent hydraulic property and the e...

This study aimed to examine the cause of latent hydraulic property manifestation of ground granulated blast-furnace slag(GGBFS) using different alkali activators in pH, type and quantity. According to the experimental result, the higher pH value accelerated lastly latent hydraulic property and the early stage strength of GCBFS was ranked as activators with the higher pH, in an order of NaOH, $Ca(OH)_{2}$ and $Na_{2}$$Co_{3}$. Also, NaOH had accelerated latent hydraulic property of GGBFS, which had 40~50% of the 3 and 7 days compressive strength of base mortar in case of using 10% of powder-weight. In the case of 30% of GGBFS substitution with annexing 2.5% $Ca(OH)_{2}$, the compressive strength on the 3 and 7 days of the early-age, was increased to 5~10% than that of the same admixture with no activator. With annexing 5.0% $Ca(OH)_{2}$, the strength was increased to 10~20%. Although activator NaOH was effective on the manifestation of latent hydraulic property, it caused cement mortar compressive strength decrease by enlarging pore diameter.