Carbon nanotubes (CNTs) have used as an electron field emitter of the field emission display (FED) due to their characteristics of high-electron emission, rapid response and low power consumption. However, to commercialize the FED with CNT emitter, some fundamental problems regarding life time and e...
Carbon nanotubes (CNTs) have used as an electron field emitter of the field emission display (FED) due to their characteristics of high-electron emission, rapid response and low power consumption. However, to commercialize the FED with CNT emitter, some fundamental problems regarding life time and emission efficiency have to be solved. In this study, we investigated the $TiO_2$ coated CNT as a field emitter. $TiO_2$ nanoparticles can coated on CNT surface by chemical solution method. $TiO_2$ nanoparticles had uniform size with the average size of about 2.4 nm to 3.1 nm. Field emission performance of CNT coated with $TiO_2$ nanoparticles was evaluated and discussed.
Carbon nanotubes (CNTs) have used as an electron field emitter of the field emission display (FED) due to their characteristics of high-electron emission, rapid response and low power consumption. However, to commercialize the FED with CNT emitter, some fundamental problems regarding life time and emission efficiency have to be solved. In this study, we investigated the $TiO_2$ coated CNT as a field emitter. $TiO_2$ nanoparticles can coated on CNT surface by chemical solution method. $TiO_2$ nanoparticles had uniform size with the average size of about 2.4 nm to 3.1 nm. Field emission performance of CNT coated with $TiO_2$ nanoparticles was evaluated and discussed.
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
이론/모형
TiO2 nanoparticles were coated on CNT surface by chemical solution method. Heterogeneous nucleation of TiO2 nanoparticles occurs on CNT surface.
성능/효과
XRD pattern of the TiO2 nanoparticle coated on CNT was shown in Fig. 2. Peaks were matched with the anatase phase TiO2 (JCPD #21-1272) but the crystallinity was slightly low. Coating quantity of TiO2 on CNT was about 46 wt% determined by TG-DTA analysis.