Abstract ▼ AI-Helper

In this paper, each specimen blended at weight proportions of 80% HDPE to 20% EVA, 70% HDPE to 30% EVA, 60% HDPE to 40% EVA, and 50% HDPE to 50% EVA was manufactured respectively. The insulation performances of the proposed insulator were compared with conventional XLPE, main insulating material of ...

In this paper, each specimen blended at weight proportions of 80% HDPE to 20% EVA, 70% HDPE to 30% EVA, 60% HDPE to 40% EVA, and 50% HDPE to 50% EVA was manufactured respectively. The insulation performances of the proposed insulator were compared with conventional XLPE, main insulating material of CV cable on the basis of the investigation results of DC insulation performances. From the space charge density, electric field and potential profiles with raising DC voltage and time variation in HE82, distortion of electric field distribution was improved. As EVA mixed into the bulks acts as nucleation in crystallization process of HDPE, the size of spherulites became decreased and finally formed continuous network structure. Ultimately it resulted from extinction of space charge in the interfacial region of spherulites.