Low temperature and dieletric properties of $Al_2O_3$/CAS glass composites by dose and particle size of $Al_2O_3$ filler and sintering time $Al_2O_3$ 충전제의 함량, 입도 및 소결시간에 따른 $Al_2O_3$/CAS glass 복합체의 저온 소결 및 유전 특성원문보기
Kim, Kwan-Soo
(강릉원주대학교)
,
Kim, Myung-Soo
(강릉원주대학교)
,
Yoon, Sang-Ok
(강릉원주대학교)
,
Park, Jong-Guk
(강원대학교)
,
Kim, So-Jung
(한중대학교)
,
Kim, In-Tae
((주)써모텍)
,
Kim, Shin
((주)써모텍)
Influences of dose and particle size of $Al_2O_3$ filler and sintering time on the dielectric properties of $Al_2O_3$ filler/CaO-$Al_2O_3-SiO_2$ (CAS) glass composites were investigated with a view to applying the composites to the substrate material in low temperatu...
Influences of dose and particle size of $Al_2O_3$ filler and sintering time on the dielectric properties of $Al_2O_3$ filler/CaO-$Al_2O_3-SiO_2$ (CAS) glass composites were investigated with a view to applying the composites to the substrate material in low temperature co-firing ceramic (LTCC) technology. The increased addition of $Al_2O_3$ filler with the particle size of 1 ${\mu}m$ monotonically decreased the density of the sintered specimen at a given temperature, while sintering of the 10 wt% $Al_2O_3$ added specimen at $925^{\circ}C$ for 2 h demonstrated 96.0 % of the relative density, dielectric constant of 6.34, and quality factor of 2,760 GHz. As for the influence of the particle size of the $Al_2O_3$ filler, there existed an optimum particle size (30 ${\mu}m$) to ensure successful densification (96.5 %) of the 10 wt% $Al_2O_3$/CAS composites at $925^{\circ}C$ for 2 h, at which condition the specimen demonstrated dielectric constant of 5.45 and quality factor of 3,740 GHz. When the influence of the sintering time of the 10 wt% $Al_2O_3$) (30 ${\mu}m$) added specimen was investigated at the sintering temperature of $925^{\circ}C$, an overly long sintering time degraded dielectric properties due to the over-sintering and the significant growth of the second phase such as anorthite, while the sintering for 4 h demonstrated 96.58 % of the relative density, dielectric constant of 5.4, and quality factor of 4,050 GHz. These results demonstrate the feasibility of the investigated material as the substrate material in LTCC technology.
Influences of dose and particle size of $Al_2O_3$ filler and sintering time on the dielectric properties of $Al_2O_3$ filler/CaO-$Al_2O_3-SiO_2$ (CAS) glass composites were investigated with a view to applying the composites to the substrate material in low temperature co-firing ceramic (LTCC) technology. The increased addition of $Al_2O_3$ filler with the particle size of 1 ${\mu}m$ monotonically decreased the density of the sintered specimen at a given temperature, while sintering of the 10 wt% $Al_2O_3$ added specimen at $925^{\circ}C$ for 2 h demonstrated 96.0 % of the relative density, dielectric constant of 6.34, and quality factor of 2,760 GHz. As for the influence of the particle size of the $Al_2O_3$ filler, there existed an optimum particle size (30 ${\mu}m$) to ensure successful densification (96.5 %) of the 10 wt% $Al_2O_3$/CAS composites at $925^{\circ}C$ for 2 h, at which condition the specimen demonstrated dielectric constant of 5.45 and quality factor of 3,740 GHz. When the influence of the sintering time of the 10 wt% $Al_2O_3$) (30 ${\mu}m$) added specimen was investigated at the sintering temperature of $925^{\circ}C$, an overly long sintering time degraded dielectric properties due to the over-sintering and the significant growth of the second phase such as anorthite, while the sintering for 4 h demonstrated 96.58 % of the relative density, dielectric constant of 5.4, and quality factor of 4,050 GHz. These results demonstrate the feasibility of the investigated material as the substrate material in LTCC technology.