Polycrystalline CdSe thin films were grown on ceramic substrate using a chemical bath deposition(CBD)method. They were annealed at various temperature and X-ray diffraction patterns were measured by X-ray diffractometer in order to study CdSe polycrystal structure. Using extrapolation method of X-ra...

Polycrystalline CdSe thin films were grown on ceramic substrate using a chemical bath deposition(CBD)method. They were annealed at various temperature and X-ray diffraction patterns were measured by X-ray diffractometer in order to study CdSe polycrystal structure. Using extrapolation method of X-ray diffraction patterns for the CdSe samples annealed in $N_2$ gas at $450^{\circ}C$ it was found hexagonal structure whose lattice parameters $a_0$ and $c_0$ were $4.302{\AA}$ and 7.014 ${\AA}$, respectively. Its grain size was about 0.3 ${\mu}m$. Hall effect on this sample was measured by Van der Pauw method and studied on carrier density and movility depending on temperature. From Hall data, the mobility was likely to be decreased by piezo electric scattering at temperature range of 33K and 200K, and by polar optical scattering at temperature range of 200K and 293K. We measured also spectral response, sensitivity$(\gamma)$, maximum allowable power dissipation and response time on these samples.