Abstract ▼ AI-Helper

MI(Magneto-Impedance) sensor which is made by thin films has significantly high detecting sensitivity in weak magnetic field. It also has a merit to be able to build in the low power system. Its structure is simple, which makes it easier to prepare a miniature. In this study, its magnetic permeabili...

MI(Magneto-Impedance) sensor which is made by thin films has significantly high detecting sensitivity in weak magnetic field. It also has a merit to be able to build in the low power system. Its structure is simple, which makes it easier to prepare a miniature. In this study, its magnetic permeability and anisotropy field$(H_k)$ as a function of a thickness of sputtered amorphous CoZrNb films with zero-magnetostriction and excellent soft magnetic property are investigated. In order to make a uniaxial anisotropy, film was subjected to the post annealing in a static magnetic field with 1KOe intensity at 250, 300, and $320^{\circ}C}$ respectively for 2 hours. Anisotropy field$(H_k)$ of film is measured by using a MH loop tracer. Its magnetic permeability of a film is measured over the frequency range from 1 MHz to 750MHz. It has shown that the magnetic permeability of amorphous CoZrNb film is decreased due to the skin effect with increasing a thickness of the CoZrNb film, and hence its driving frequency is lowered. And, it was examined on the permeability and impedance to fabricate the MI sensor which acts at a low frequency by thickening a CoZrNb film relatively.