This paper presents the electrical characteristics of metal oxide varistors for lightning surge arresters. ZnO varistors were fabricated with typical ceramic production methods and two types of varistors were also prepared to be compared. The nominal discharge current and line discharge class of tho...

This paper presents the electrical characteristics of metal oxide varistors for lightning surge arresters. ZnO varistors were fabricated with typical ceramic production methods and two types of varistors were also prepared to be compared. The nominal discharge current and line discharge class of those varistors are $10kA(8/20{\mu}s)$ and class 3, respectively. The diameter of varistors manufactured and prepared were in the range of 61.6~65.0mm and the thickness of those were in the range of 27~42.52mm. The reference and residual voltage were tested and reference and residual voltage per 1mm and the ratio of reference and residual voltage were calculated. The reference voltage per 1mm of varistors manufactured was about 175V/mm but that of A's and B's varistors was nearly 200V/mm. The residual voltage exhibited the same trends as the reference voltage, so the reference and residual voltage per 1mm of domestic varistors should be increased. According to the results of tests, it is thought that if the reference and residual voltage per 1mm were increased to 200V/mm and 330V/mm, domestic ZnO varistors would be possible to apply to the station class arresters in the near future.