Eutectic composition phase with low melting point which solidifies at the final stage affects the solidification cracking at the intercellular or interdendritic area of welds and castings. If sufficient amount of eutectic composition liquid does not exist between the solidifying phases, the disconti...

Eutectic composition phase with low melting point which solidifies at the final stage affects the solidification cracking at the intercellular or interdendritic area of welds and castings. If sufficient amount of eutectic composition liquid does not exist between the solidifying phases, the discontinuities remain as cracks. However, abundant amount of liquid eutectic composition existing in the final stage can flow into the discontinuities easily and heal the cracks. By flowing of liquid eutectic and healing of discontinuities, the possibility of cracking can be reduced when the amount of eutectic liquid is sufficient. For the solidification of pure metals, liquid eutectic does not exist and the interlocking of growing solid phases can be realized without interruption of liquid film. Therefore there is little possibility of solidification cracking in the case of welds and castings of pure metal. In a practical sense, the effective way to reduce or prevent the solidification cracking is making the composition of molten pool or melts near to the eutectic composition.