As the damage to fine dust increased, the Republic of Korea designated fine dust as a social disaster. The composition of the fine dust is composed of carbon, sulfate, nitrate, ammonium and minerals. The cause of fine dust is naturally generated by dirt, pollen, etc. In addition, there are artificia...
As the damage to fine dust increased, the Republic of Korea designated fine dust as a social disaster. The composition of the fine dust is composed of carbon, sulfate, nitrate, ammonium and minerals. The cause of fine dust is naturally generated by dirt, pollen, etc. In addition, there are artificial causes such as gaseous vehicle exhaust gas emitted from the use of fossil fuel. When fine dust enters the human body through breathing, it causes various respiratory diseases and skin diseases. In IARC, fine dust was designated as a carcinogen group 1. In this research, we tried to adsorb fine dust by physical adsorption using powdered activate carbon. Powdered activate carbon is a powdered activated carbon activated in a carbonized state. Porous material with high specific surface area and low density. Experimental items were tested for density, water absorption, and fine dust concentration according to the PAC addition ratio. Basic experiments were carried out to fabricate the fine dust adsorption matrix.
As the damage to fine dust increased, the Republic of Korea designated fine dust as a social disaster. The composition of the fine dust is composed of carbon, sulfate, nitrate, ammonium and minerals. The cause of fine dust is naturally generated by dirt, pollen, etc. In addition, there are artificial causes such as gaseous vehicle exhaust gas emitted from the use of fossil fuel. When fine dust enters the human body through breathing, it causes various respiratory diseases and skin diseases. In IARC, fine dust was designated as a carcinogen group 1. In this research, we tried to adsorb fine dust by physical adsorption using powdered activate carbon. Powdered activate carbon is a powdered activated carbon activated in a carbonized state. Porous material with high specific surface area and low density. Experimental items were tested for density, water absorption, and fine dust concentration according to the PAC addition ratio. Basic experiments were carried out to fabricate the fine dust adsorption matrix.
* AI 자동 식별 결과로 적합하지 않은 문장이 있을 수 있으니, 이용에 유의하시기 바랍니다.
문제 정의
본 연구에서는 분말활성탄를 활용한 흡착형 경화체의 특성을 분석하기 위하여 시멘트 기반 분말활성탄 첨가율에 따른 실험을 진행하였다. 분말활성탄은 나무 등이 탄화된 상태에서 활성시킨 활성탄을 분말화한 것이며, 1,100㎡ /g 이상의 비표면적을 가지는 다공질 재료이다.
실험항목으로는 밀도, 흡수율 및 압축강도를 측정하였다. 실험요인 및 수준은 표 1과 같으며, 본 실험은 흡착 성능을 검토하기전 기초 실험으로써 경화체의 물리적 특성을 검토하고자 하였다.
제안 방법
시멘트 기반으로 흡착형 경화체를 제작하였으며, W/B는 50%로 고정한 뒤 분말활성탄 첨가율은 0, 10, 20, 30, 40(%)등 총 5가지 수준으로 진행하였다. 실험항목으로는 밀도, 흡수율 및 압축강도를 측정하였다.
시멘트 기반으로 흡착형 경화체를 제작하였으며, W/B는 50%로 고정한 뒤 분말활성탄 첨가율은 0, 10, 20, 30, 40(%)등 총 5가지 수준으로 진행하였다. 실험항목으로는 밀도, 흡수율 및 압축강도를 측정하였다. 실험요인 및 수준은 표 1과 같으며, 본 실험은 흡착 성능을 검토하기전 기초 실험으로써 경화체의 물리적 특성을 검토하고자 하였다.
대상 데이터
분말활성탄은 나무 등이 탄화된 상태에서 활성시킨 활성탄을 분말화한 것이며, 1,100㎡ /g 이상의 비표면적을 가지는 다공질 재료이다. 본 연구에서 사용된 분말활성탄의 밀도 0.43g/㎤인 것을 사용하였다.
성능/효과
분말활성탄을 사용할 경우 밀도와 흡수율은 반비례의 관계를 나타났다. 또한 미세먼지 농도는 감소하였으며, 분말활성탄의 높은 비표면적에 의한 물리적 흡착이 이루어지는 것으로 분석된다.
시멘트 기반 분말활성탄 첨가율에 따른 흡착형 경화체의 실험결과는 다음과 같다. 분말활성탄 첨가율이 증가함에 따라 밀도는 감소하며, 흡수율은 증가하였다. 분말활성탄을 사용할 경우 밀도와 흡수율은 반비례의 관계를 나타났다.