Process for the production of niobium oxide powder for use in capacitors
원문보기
IPC분류정보
국가/구분
United States(US) Patent
공개
국제특허분류(IPC7판)
C01G-031/02
C01G-031/00
출원번호
US-0573293
(2004-01-23)
공개번호
US-0275204
(2006-12-07)
우선권정보
BR-PI 0301252-9(2003-09-25)
국제출원번호
PCT/BR04/000003
(2004-01-23)
발명자
/ 주소
Tagusagawa,Solon
Ono,Alberto
Beneduce,Flavio
Ferreira,Joao
출원인 / 주소
COMPANHIA BRASILEIRA DE METALURGIA E MINERACAO
IP INSTITUTO DE PESQUISAS TECHNOLOGICAS DO ESTADO DE SAO PAULO S/A
대리인 / 주소
BIRCH STEWART KOLASCH &
인용정보
피인용 횟수 :
0인용 특허 :
0
초록▼
The present invention is related to a process for the production of a powder of niobium monoxide (NbO) having a high purity, large specific surface area, controlled oxygen and nitrogen contents and a morphology adequate for use in the manufacture of capacitors, characterized by comprising two niobiu
The present invention is related to a process for the production of a powder of niobium monoxide (NbO) having a high purity, large specific surface area, controlled oxygen and nitrogen contents and a morphology adequate for use in the manufacture of capacitors, characterized by comprising two niobium pentoxide (Nb2O5 ) reduction steps, the first step comprising reducing, by hydrogen, the niobium pentoxide (Nb2O5) to niobium dioxide (NbO 2), and the second step comprising reducing niobium dioxide (NbO 2) to niobium monoxide (NbO), by using an oxygen getter material in a convenient atmosphere which permits the transfer of the oxygen atoms from the niobium oxide (NbO2) to the getter material, under adequate conditions of time and temperature to form the niobium monoxide (NbO). The particles of powder of niobium monoxide (NbO) produced using the instant process are small, have a large surface area and an appropriate morphology, and are adequate for the production of capacitors.
대표청구항▼
1. A process for the production niobium monoxide powder characterized by comprising two reduction steps of niobium oxide, the first step comprises reducing by hydrogen of niobium pentoxide to niobium dioxide, and the second step comprises reducing niobium dioxide to niobium monoxide, by using an ox
1. A process for the production niobium monoxide powder characterized by comprising two reduction steps of niobium oxide, the first step comprises reducing by hydrogen of niobium pentoxide to niobium dioxide, and the second step comprises reducing niobium dioxide to niobium monoxide, by using an oxygen getter material and in an atmosphere which allows the transfer of the oxygen atoms from the niobium dioxide to the getter material, wherein the getter material can be a refractory metal or a reactive metal or a refractory metal or a reactive metal hydride. 2. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the first reduction step is conducted at a temperature between 700° C. and 1500° C., and preferably between 800° C. and 1200° C., for periods of time varying from 15 to 300 minutes, and preferably between 30 and 180 minutes. 3. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the first reduction step is conducted in an atmosphere of hydrogen gas or a combination of hydrogen gas and other inert gasses at various ratios, such as, argon, helium and nitrogen. 4. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the first reduction step is conducted in an atmosphere of carbon monoxide or any other gas or gaseous mixture having an adequate reducing potential. 5. A process for the production of niobium monoxide powder, according to claim 1 characterized by producing in the first reduction step the niobium dioxide with a microporous structure, with a specific surface area between 0.5 m2/g and 20 m2/g. 6. A process for the production of niobium monoxide powder, according to claim 1, characterized by producing in the first reduction step the niobium dioxide with a microporous structure, with at least 41 percent porosity. 7. A process for the production of niobium monoxide powder, according to claim 1, characterized by producing in the first reduction step the niobium dioxide with a microporous structure, with low residual content of niobium pentoxide. 8. A process for the production of niobium monoxide powder, according to claim 1, characterized by using in the second reduction step the niobium dioxide with a specific surface area between 0. 5 and 20 m2/g. 9. A process for the production of niobium monoxide powder, according to claim 1, characterized by using in the second reduction step the niobium dioxide with at least 41 percent porosity. 10. A process for the production of niobium monoxide powder, according to claim 1, characterized by using as oxygen getter material in the second reduction step the niobium metal and alloys thereof, and/or niobium metal and its alloys hydride thereof in the form of powder. 11. A process for the production of niobium monoxide powder, according to claim 1, characterized by using as oxygen getter material in the second reduction step the tantalum metal and alloys thereof, and/or tantalum metal and its alloys hydride thereof in the form of powder. 12. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the atmosphere that allows the transfer of the oxygen atoms in the second reduction step is comprised of hydrogen gas, and may contain other gasses that do not lower the reducing potential of the hydrogen gas. 13. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the atmosphere of the second reduction step is comprised of hydrogen gas and nitrogen in such a way that allow the nitrogen doping of the formed niobium monoxide. 14. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the second reduction step is conducted at a temperature between 1000° C. and 1700° C., and preferably between 1200° C. and 1600° C., for periods of time between 10 minutes and 720 minutes, and preferably between 30 minutes and 360 minutes. 15. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the niobium monoxide that is produced does not contain detectable residual amounts of niobium dioxide or metallic niobium by X-ray diffraction. 16. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the niobium monoxide produced in the second reduction step has similar morphology of the niobium dioxide. 17. A process for the production of niobium monoxide powder, according to claim 1, characterized in that the niobium monoxide produced in the second reduction step has an atomic ratio between niobium and oxygen between 1:0.6 e 1:1.5 and preferably an atomic ratio between niobium and oxygen between 1:0.7 and 1:1.1. 18. Niobium monoxide, produced in accordance with claim 1, characterized by presenting a residual content of up to 5 percent of niobium dioxide. 19. Niobium monoxide, produced in accordance with claim 1, characterized by presenting a residual content of up to 5 percent of niobium metal. 20. Niobium monoxide, produced in accordance with claim 1, characterized by presenting a residual content of up to 5 percent of niobium dioxide and a residual content of up to 5 percent of niobium metal. 21. Niobium monoxide, produced in accordance with claim 1, characterized by having a specific surface area from 0.5 to 20.0 m2/g, preferably from 0.8 to 6.0 m2/g. 22. Niobium monoxide, produced in accordance with claim 1, characterized by having a microporous structure with at least 41 percent porosity. 23. A capacitor, manufactured with niobium monoxide produced according to claim 1, characterized by having a capacitance between 50,000 CV/g and 200,000 CV/g. 24. A capacitor, manufactured with the niobium monoxide produced according to claim 1, characterized by having a leakage current value below 1.0 nA/CV