CONCRETE OPTIMIZED FOR HIGH WORKABILITY AND HIGH STRENGTH TO CEMENT RATIO
원문보기
IPC분류정보
국가/구분
United States(US) Patent
공개
국제특허분류(IPC7판)
C04B-018/06
C04B-018/04
C04B-014/06
C04B-014/02
C04B-014/00
C04B-014/00
C04B-024/24
C04B-024/00
출원번호
US-0247388
(2008-10-08)
공개번호
US-0158966
(2009-06-25)
발명자
/ 주소
Andersen, Per Just
Hodson, Simon K.
출원인 / 주소
iCRETE, LLC
대리인 / 주소
Patent Docket Department
인용정보
피인용 횟수 :
0인용 특허 :
0
초록▼
A concrete composition having a 28-day design compressive strength of 3000 psi and a slump of about 5 inches is optimized to have high workability and a high strength to cement ratio. The concrete composition contains about 340 pounds per cubic yard hydraulic cement (e.g. Portland cement), about 102
A concrete composition having a 28-day design compressive strength of 3000 psi and a slump of about 5 inches is optimized to have high workability and a high strength to cement ratio. The concrete composition contains about 340 pounds per cubic yard hydraulic cement (e.g. Portland cement), about 102 pounds per cubic yard pozzolanic material (e.g., Type C fly ash), about 1757 pounds per cubic yard fine aggregate (e.g., FA-2 sand), about 1452 pounds per cubic yard coarse aggregate (e.g., CA-11 state rock, ¾ inch), and about 294 pounds per cubic yard water (e.g., potable water). Workability and strength to cement ratio were increased compared to one or more preexisting concrete compositions having the same 28-day design compressive strength and similar slump by optimizing the ratio of fine aggregate to coarse aggregate. The concrete composition is further characterized by high cohesiveness, resulting in relatively little or no segregation or bleeding.
대표청구항▼
What is claimed is: 1. A concrete composition having high workability and a high strength to cement ratio, comprising: hydraulic cement in an amount of 340±5% pounds per cubic yard; a pozzolanic material in an amount of 102±5% pounds per cubic yard; a fine aggregate in an amount of 1757±5% pounds p
What is claimed is: 1. A concrete composition having high workability and a high strength to cement ratio, comprising: hydraulic cement in an amount of 340±5% pounds per cubic yard; a pozzolanic material in an amount of 102±5% pounds per cubic yard; a fine aggregate in an amount of 1757±5% pounds per cubic yard; a coarse aggregate in an amount of 1452±5% pounds per cubic yard; and water in an amount of 294±5% pounds per cubic yard. 2. A concrete composition as in claim 1, the concrete composition having a 28-day compressive strength of at least about 3000 psi and a slump of at least about 5 inches as measured using a 12 inch slump cone according to ASTM C143. 3. A concrete composition as in claim 1, wherein: the hydraulic cement is included in an amount of 340±3% pounds per cubic yard; the pozzolanic material is included in an amount of 102±3% pounds per cubic yard; the fine aggregate is included in an amount of 1757±3% pounds per cubic yard; the coarse aggregate is included in an amount of 1452±3% pounds per cubic yard; and the water is included in an amount of 294±3% pounds per cubic yard. 4. A concrete composition as in claim 1, wherein: the hydraulic cement is included in an amount of 340±2% pounds per cubic yard; the pozzolanic material is included in art amount of 102±2% pounds per cubic yard; the fine aggregate is included in an amount of 1757±2% pounds per cubic yard; the coarse aggregate is included in an amount of 1452±2% pounds per cubic yard; and the water is included in an amount of 294±2% pounds per cubic yard. 5. A concrete composition as in claim 1, wherein: the hydraulic cement is included in an amount of 340±1% pounds per cubic yard; the pozzolanic material is included in an amount of 102±1% pounds per cubic yard; the fine aggregate is included in an amount of 1757±1% pounds per cubic yard; the coarse aggregate is included in an amount of 1452±1% pounds per cubic yard; and the water is included in an amount of 294±1% pounds per cubic yard. 6. A concrete composition as in claim 1, the hydraulic cement consisting essentially of Type I and/or Type II Portland cement. 7. A concrete composition as in claim 1, the pozzolanic material consisting essentially of Type C fly ash. 8. A concrete composition as in claim 1, the fine aggregate consisting essentially of sand and the coarse aggregate consisting essentially of rock. 9. A concrete composition as in claim 6, the sand consisting essentially of FA-2 sand and the rock consisting essentially of CA-11 state rock, ¾ inch. 10. A concrete composition as in claim 1, further comprising an amount of plasticizer that increases slump and decreases viscosity without causing significant segregation or bleeding of the concrete composition. 11. A concrete composition as in claim 1, further comprising one or more admixtures selected from the group consisting of air entraining agents, strength enhancing amines, dispersants, viscosity modifiers, set accelerators, set retarders, corrosion inhibitors, pigments, wetting agents, water soluble polymers, rheology modifying agents, water repellents, fibers, permeability reducers, pumping aids, fungicidal admixtures, germicidal admixtures, insecticidal admixtures, finely divided mineral admixtures, alkali reactivity reducer, and bonding admixtures. 12. A concrete composition as in claim 1, the concrete composition comprising about 2% by volume entrained air. 13. A concrete composition having high workability and a high strength to cement ratio, comprising: Type I and/or Type II Portland cement in an amount of 340±3% pounds per cubic yard; Type C fly ash in an amount of 102±3% pounds per cubic yard; sand in an amount of 1757±3% pounds per cubic yard; rock in an amount of 1452±3% pounds per cubic yard; and water in an amount of 294±3% pounds per cubic yard, the concrete composition having a 28-day design compressive strength of 3000 psi and a slump of at least about 5 inches as measured using a 12 inch slump cone according to ASTM C143. 14. A concrete composition having high workability and a high strength to cement ratio, comprising: Type I and/or Type II Portland cement in an amount of 340±2% pounds per cubic yard; Type C fly ash in an amount of 102 pounds±2% per cubic yard; sand in an amount of 1757 pounds±2% per cubic yard; rock in an amount of 1452 pounds±2% per cubic yard; and water in an amount of 294 pounds±2% per cubic yard, the concrete composition having a 28-day design compressive strength of 3000 psi and a slump of at least about 5 inches as measured using a 12 inch slump cone according to ASTM C143. 15. A concrete composition having high workability and a high strength to cement ratio, comprising: Type I and/or Type II Portland cement in an amount of 340±1% pounds per cubic yard; Type C fly ash in an amount of 102 pounds±1% per cubic yard; sand in an amount of 1757 pounds±1% per cubic yard; rock in an amount of 1452 pounds±1% per cubic yard; and water in an amount of 294 pounds±1% per cubic yard, the concrete composition having a 28-day design compressive strength of 3000 psi and a slump of at least about 5 inches as measured using a 12 inch slump cone according to ASTM C143.