초록 ▼

Disclosed herein are a soft magnetic metal powder having a pearlite lamellar structure in which ferrite structures and cementite structures are repeated, a method for preparing the same, and an electronic component including the same as a core material. According to the present invention, the soft m

Disclosed herein are a soft magnetic metal powder having a pearlite lamellar structure in which ferrite structures and cementite structures are repeated, a method for preparing the same, and an electronic component including the same as a core material. According to the present invention, the soft magnetic metal powder having the pearlite lamellar structure in which the ferrite structures and the cementite structures are repeated may be easily prepared, and an eddy current loss may be easily decreased without changing the existing molding process, such that the soft magnetic metal powder may be used as a core material of various electronic components such as an inductor, a motor, an actuator, a sensor, a transformer, and a reactor, requiring soft magnetic properties.

대표청구항 ▼

1. A soft magnetic metal powder having a pearlite lamellar structure in which ferrite structures and cementite structures are repeated. 2. The soft magnetic metal powder according to claim 1, wherein the ferrite structure is made of α-Fe. 3. The soft magnetic metal powder according to claim 1, where

1. A soft magnetic metal powder having a pearlite lamellar structure in which ferrite structures and cementite structures are repeated. 2. The soft magnetic metal powder according to claim 1, wherein the ferrite structure is made of α-Fe. 3. The soft magnetic metal powder according to claim 1, wherein the cementite structure is made of Fe3C. 4. The soft magnetic metal powder according to claim 1, wherein a particle size of the soft magnetic metal powder is 1 to 100 μm. 5. The soft magnetic metal powder according to claim 1, wherein the ferrite structure and the cementite structure are controlled by a carbon content. 6. The soft magnetic metal powder according to claim 5, wherein the carbon content is 2 wt % or less based on a content of an α-Fe powder forming the ferrite structure. 7. The soft magnetic metal powder according to claim 1, wherein it is usable at a high frequency of 0.1 to 30 MHz. 8. A method for preparing a soft magnetic metal powder having a pearlite lamellar structure in which ferrite structures and cementite structures are repeated, the method comprising: infiltrating carbon into an α-Fe powder; andheat-treating the α-Fe powder having the carbon infiltrated thereinto. 9. The method according to claim 8, wherein the carbon is infiltrated in a content of 2 wt % or less based on a content of the α-Fe powder. 10. The method according to claim 8, wherein the heat-treating is performed at 740 to 800. 11. The method according to claim 8, wherein the ferrite structure is made of α-Fe. 12. The method according to claim 8, wherein the cementite structure is made of Fe3C formed by combining the α-Fe powder and the carbon with each other. 13. An electronic component comprising the soft magnetic metal powder according to claim 1 as a core material. 14. The electronic component according to claim 13, wherein it is any one selected from an inductor, a motor, an actuator, a sensor, a transformer, and a reactor.