The invention concerns a method for producing a three-dimensional object, in particular an artificial tooth, by stereolithography wherein a liquid photocurable resin composition is cured by light. Said photocurable resin composition contains, based on the total weight of the photocurable resin compo
The invention concerns a method for producing a three-dimensional object, in particular an artificial tooth, by stereolithography wherein a liquid photocurable resin composition is cured by light. Said photocurable resin composition contains, based on the total weight of the photocurable resin composition, (i) from 90 to 99.9% by weight of a radical polymerizable organic compound (A) selected from radical polymerizable monomers, oligomers, pre-polymers and mixtures thereof; and (ii) from 0.1 to 10% by weight of a photosensitive radical polymerization initiator (B). Said radical polymerizable organic compound (A) comprises, based on the weight of the radical polymerizable organic compound (A), from 0.5 to 20% by weight of a polyrotaxane compound comprising a polymer chain selected from polyethylene glycol (PEG), polypropylene glycol (PPG), polyethylene glycol-polypropylene glycol (PEG-PPG) block copolymer or polydimethylsiloxane (PDMS), onto which the cyclodextrin ring(s) is/are slipped and wherein the cyclodextrin is derivatized with at least a radical polymerizable group. The invention also concerns a relative liquid photocurable resin composition and articles produced thereby.
대표청구항▼
1) Method for producing a three-dimensional object by stereolithography wherein a liquid photocurable resin composition is cured by light, said photocurable resin composition containing: (i) from 90 to 99.9% by weight, based on the total weight of the photocurable resin composition, of a radical pol
1) Method for producing a three-dimensional object by stereolithography wherein a liquid photocurable resin composition is cured by light, said photocurable resin composition containing: (i) from 90 to 99.9% by weight, based on the total weight of the photocurable resin composition, of a radical polymerizable organic compound (A) selected from radical polymerizable monomers, oligomers, pre-polymers and mixtures thereof;(ii) from 0.1 to 10% by weight, based on the total weight of the photocurable resin composition, of a photosensitive radical polymerization initiator (B);wherein said radical polymerizable organic compound (A) comprises, based on the weight of the radical polymerizable organic compound (A), from 0.5 to 20% by weight of a polyrotaxane compound having the following general formula (I): whereinZ is a bulky capping group, preferably selected from adamantane and its derivatives, 2,4-dinitrophenyl, or cyclodextrin and its derivatives;the dotted line ------ is a polymer chain selected from the group consisting of polyethylene glycol (PEG), polypropylene glycol (PPG), polyethylene glycol-polypropylene glycol (PEG-PPG) block copolymer or polydimethylsiloxane (PDMS), onto which the cyclodextrin ring(s) is/are slipped;m is an integer and independently represents the number of glucose units in the cyclodextrin ring, preferably m=6, 7 or 8;n is an integer and represents the number of cyclodextrin rings;X is independently H, or a radical polymerizable group, such as a methacryloyl-containing group or an acryloyl-containing group, with the condition that at least one X is a radical polymerizable group. 2) Method according to claim 1, characterized in that it comprises the following steps: (a) accommodating said liquid photocurable resin composition in a shaping container having a light permeable bottom face, and irradiating the photocurable resin composition in the shaping container with light in a predetermined shape pattern through the light permeable bottom face of the shaping container in accordance with slice data, every one layer based on three-dimensional CAD data to form a cured resin layer having a predetermined shape pattern for one layer;(b) lifting up the cured resin layer for one layer formed during step (a), thereby allowing the liquid photocurable resin composition to flow into the space between the lower face of the cured resin layer and the bottom face of the shaping container, and irradiating the photocurable resin composition between the lower face of the cured resin layer and the bottom face of the shaping container with light in a predetermined shape pattern through the light permeable bottom face of the shaping container in accordance with slice data, every one layer based on three-dimensional CAD data to form a further cured resin layer having a predetermined shape pattern for one layer, and(c) repeating the operation of step (b) until the desired object is obtained. 3) The method according to claim 2, characterized in that the three-dimensional CAD data are obtained using a computed tomography device (CT device), a magnetic resonance imaging device (MRI), a computed radiographic device (CR device), or an intraoral 3D scanner. 4) Method according to claim 1, characterized in that the radical polymerizable group of said liquid photocurable resin composition is constituted by a methacryloyl or acryloyl-containing unit bonded by a spacer unit to said cyclodextrin ring. 5) Liquid photocurable resin composition for stereolithography, containing: (i) from 90 to 99.9% by weight, based on the total weight of the photocurable resin composition, of a radical polymerizable organic compound (A) selected from radical polymerizable monomers, oligomers, pre-polymers and mixtures thereof;(ii) from 0.1 to 10% by weight, based on the total weight of the photocurable resin composition, of a photosensitive radical polymerization initiator (B);wherein said radical polymerizable organic compound (A) comprises, based on the weight of the radical polymerizable organic compound (A), from 0.5 to 20% by weight of a polyrotaxane compound having the following general formula (I): whereinZ is a bulky capping group, preferably selected from adamantane and its derivatives, 2,4-dinitrophenyl, or cyclodextrin and its derivatives;the dotted line ------ is a polymer chain selected from the group consisting of polyethylene glycol (PEG), polypropylene glycol (PPG), polyethylene glycol-polypropylene glycol (PEG-PPG) block copolymer or polydimethylsiloxane (PDMS), onto which the cyclodextrin ring(s) is/are slipped;m is an integer and independently represents the number of glucose units in the cyclodextrin ring, preferably m=6, 7 or 8;n is an integer and represents the number of cyclodextrin rings;X is independently H, or a radical polymerizable group, such as a methacryloyl-containing group or an acryloyl-containing group, with the condition that at least one X is a radical polymerizable group. 6) The liquid photocurable resin composition according to claim 5, characterized in that said radical polymerizable group is constituted by a methacryloyl or acryloyl-containing unit bonded by a spacer unit to said cyclodextrin ring. 7) The liquid photocurable resin composition according to claim 6, characterized in that said radical polymerizable group is independently selected from —[(C═O)(CH2)5O—]p—CONH(CH2)2CO2C(R1)═CH2 or—CH2CHMeO—[(C═O)(CH2)5O—]q—CONH(CH2)2CO2C(R1)═CH2, wherein R1 represents a hydrogen atom or a methyl group with p and q being integers indicating the number of repeating units. 8) The liquid photocurable resin composition according to claim 5, characterized in that said radical polymerizable organic compound (A) further comprises: (i) a urethane-based di(meth)acrylate compound (A-1a) obtained by the reaction of 1 mol of an organic diisocyanate compound with 2 mol of hydroxyalkyl (meth)acrylate, represented by the following general formula (A-1a): D-{NH—CO—O—R2—O—CO—C(R1)═CH2}2 (A-1a) wherein R1 represents a hydrogen atom or a methyl group, R2 represents an alkylene group, and D represents an organic diisocyanate compound residue; and/or (ii) a di(meth)acrylate compound (A-1b) obtained by the reaction of 1 mol of a diepoxy compound with 2 mol of (meth)acrylic acid, represented by the following general formula (A-1b): E-{C(H)(OH)—CH2—O—CO—C(R3)═CH2}2 (A-1b) wherein R3 represents a hydrogen atom or a methyl group, and E represents a diepoxy compound residue. 9) The liquid photocurable resin composition according to claim 5, characterized in that the viscosity of said photocurable resin composition is 20,000 mPa·s or less, more preferably 15,000 mPa·s or less, and still more preferably 10,000 mPa·s or less, when measured at 25° C. according to method ISO 2555 with a single cylinder rotational viscometer. 10) The liquid photocurable resin composition according to claim 5, characterized in that every radical polymerizable organic compound (A) is a methacrylate-based compound. 11) The liquid photocurable resin composition according to claim 5, characterized in that in said polyrotaxane compound the polymer chain is polyethylene glycol, the cyclodextrin is α-cyclodextrin and the bulky groups are —NH-adamantane. 12) The liquid photocurable resin composition according to claim 5, characterized in that said radical polymerizable organic compound (A) further includes a viscosity reducing compound (A-2) which is at least one of a methacrylic acid ester, an acrylic acid ester, a polyester methacrylate, a polyester acrylate, a polyether methacrylate of alcohols, a polyether acrylate of alcohols. 13) The liquid photocurable resin composition according to claim 5, characterized in that said radical polymerizable organic compound (A) other than the polyrotaxane compound and other than compounds (A-1a), (A-1b) and (A-2) is selected from radical polymerizable monomers. 14) The liquid photocurable resin composition according to claim 5, characterized in that said photocurable resin composition is blended with 10 to 250 parts per weight of a filler (C) per every 100 parts per weight of said photocurable resin composition. 15) The liquid photocurable resin composition according to claim 5, characterized in that said filler (C) is selected from a silica powder, an alumina powder, a zirconia powder, a glass powder, powders prepared by treating the above powders with a coupling agent, and mixtures thereof. 16) A three-dimensional article comprising a photo-cured resin composition obtained by the method according to claim 1. 17) The three-dimensional article according to claim 16, characterized in that said three-dimensional article is an artificial tooth.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.