초록 ▼

A particular elastomeric polyurethane polymer is heated to about 225°C. to ensure complete melting prior to extrusion side-by-side with a molten hard polymer. The polyurethane polymer is made from an aromatic diisocyanate, a high molecular weight (800-3000) diol and a low molecular weight (500 or le

A particular elastomeric polyurethane polymer is heated to about 225°C. to ensure complete melting prior to extrusion side-by-side with a molten hard polymer. The polyurethane polymer is made from an aromatic diisocyanate, a high molecular weight (800-3000) diol and a low molecular weight (500 or less) diol, combined in specific ratio ranges.

대표청구항 ▼

A process for preparing a conjugate fiber, comprising: a. preparing a solid melt-spinnable fiber-forming polyurethane by reacting together 1. a polymeric glycol having a molecular weight between 800 and 3000, 2. between 4.6 and 8.8 mols of an aromatic diisocyanate per mol of said polymeric glycol,

A process for preparing a conjugate fiber, comprising: a. preparing a solid melt-spinnable fiber-forming polyurethane by reacting together 1. a polymeric glycol having a molecular weight between 800 and 3000, 2. between 4.6 and 8.8 mols of an aromatic diisocyanate per mol of said polymeric glycol, and 3. sufficient low molecular weight polyol to provide an NCO/OH ratio between 0.96 and 1.04 to 1; b. heating said polyurethane to a temperature within the range from at least mols diisocyanate 210.6 +3 °C. mols polymeric glycol and less than 255°C. to form a first molten stream; c. maintaining the temperature of said first molten stream within said range for a treatment period of at least 10 seconds and less than a treatment period which would cause objectionable degradation; d. combining said first molten stream with a second molten stream in a side-by-side conjugate relationship to form a conjugated stream, said second molten stream being formed from a melted fiber-forming hard polymer; e. extruding said conjugated stream through a spinneret orifice; and f. cooling said conjugated stream to form a conjugate yarn.