초록 ▼

A white, bright and opaque urea formaldehyde pigment is prepared in a continuous process by precipitating a urea formaldehyde resin or prepolymer having a relatively low water tolerance and a relatively high viscosity in an aqueous precipitating bath containing an acid catalyst. The reaction is carr

A white, bright and opaque urea formaldehyde pigment is prepared in a continuous process by precipitating a urea formaldehyde resin or prepolymer having a relatively low water tolerance and a relatively high viscosity in an aqueous precipitating bath containing an acid catalyst. The reaction is carried out by supplying the urea formaldehyde resin to one or more reactors each containing the precipitating bath at an elevated temperature and under agitation, wherein a precipitate begins to form almost immediately. The reaction is allowed to progress for a length of time sufficient to permit most of the higher molecular weight fractions of the resin to precipitate out, the precipitate is then filtered preferably at the reaction temperature, washed and collected. Meanwhile, the filtrate from the reaction is recycled back through the reactor or reactors whereupon additional urea formaldehyde resin is added along with an effective amount of a synthetic polymeric flocculant to assist in converting the lower molecular weight fractions of the resin in the recycled filtrate into a useful product. The synthetic polymeric flocculant also controls the solids content and optical efficiency of the precipitate produced.

대표청구항 ▼

A continuous process for manufacturing a white, bright and opaque precipitated urea formaldehyde pigment comprising: (a) supplying on a continuous basis, a urea formaldehyde resin to a plurality of serially connected reaction vessels, said resin having a water tolerance of from about 1.5 to 5.0 and

A continuous process for manufacturing a white, bright and opaque precipitated urea formaldehyde pigment comprising: (a) supplying on a continuous basis, a urea formaldehyde resin to a plurality of serially connected reaction vessels, said resin having a water tolerance of from about 1.5 to 5.0 and a viscosity of at least about 450 cps at 50% solids, each of said reaction vessels being precharged with an aqueous acid catalyst precipitating bath containing from about 0.125 to 1.5% by volume of a strong mineral acid at a temperature of from about 20°-95°C., (b) reacting the mixture of resin and precipitating bath in said reaction vessels at a resin to water ratio of from about 1:16 to 3:8 under agitation for a period of time of from about ½to 5 hours including the time for addition of the resin to the precipitating bath to permit most of the higher molecular weight fractions of the resin to react and precipitate in the precipitating bath; (c) filtering the precipitated pigment product formed in step (b) from the precipitating bath at a temperature of from about 25°to 70°C., (d) recycling, on a continuous basis the filtrate obtained from step (c), containing the unreacted lower molecular weight fractions of the resin, back into said reaction vessels; and, (e) introducing into the recycled filtrate after each filtering step from about 0.01% to about 0.5% by weight based on the solids of the urea formaldehyde resin supplied to said reaction vessels of a flocculant material selected from the group consisting of a hydrophilic colloid having a molecular weight in the range of from about 100,000 to 100,000,000 and a functional group selected from the class consisting of hydroxyl, carboxylic, amide, amine and quaternary compounds, and acrylamide.