초록 ▼

A flame-retardant pressure-sensitive adhesive composition that is compatible with enameled magnet wire is provided by adding to a base adhesive material certain halogenated organic compounds, such as decabromodiphenyl oxide, which exhibit little halogen or other loss upon exposure to elevated temper

A flame-retardant pressure-sensitive adhesive composition that is compatible with enameled magnet wire is provided by adding to a base adhesive material certain halogenated organic compounds, such as decabromodiphenyl oxide, which exhibit little halogen or other loss upon exposure to elevated temperature.

대표청구항 ▼

A flame-retardant pressure-sensitive adhesive composition for use on electrically insulating tape that is compatable, as defined herein, with magnet wire insulation, said adhesive composition providing, when applied in a 5-mil-thickness on a polyester film backing, at least 20 ounces of adhesion to

A flame-retardant pressure-sensitive adhesive composition for use on electrically insulating tape that is compatable, as defined herein, with magnet wire insulation, said adhesive composition providing, when applied in a 5-mil-thickness on a polyester film backing, at least 20 ounces of adhesion to steel per inch width, and said adhesive composition comprising (1) a base pressure-sensitive adhesive material that exhibits no more than about 3 weight-percent halogen loss after weeks at 175°C and (2) at least 2.5 weight-percent of halogenated organic material that (a) is halogenated with either chlorine or bromine atoms that together constitute at least 40 weight-percent of the organic material, (b) exhibits no more than about 1 weight-percent loss when heated to 200°C in a thermogravimetric analysis performed by raising the temperature of the organic material from room temperature at a rate of 40°C/minute, (c) exhibits no more than about 3 weight-percent halogen loss after two weeks at 175°C, (d) exhibits less than 10 percent loss in overall weight after two weeks at 175°C and (e) comprises less than about 50 weight-percent of said adhesive composition. A flame-retardant electrically insulating pressure-sensitive adhesive tape which is compatible, as defined herein, wiTh magnet wire insulation and exhibits at least 20 ounces of adhesion to steel per inch width, comprising a flexible backing and at least one layer of pressure-sensitive adhesive composition united to the backing, said adhesive composition comprising (1) a base pressure-sensitive adhesive material that exhibits less than about 3 weight-percent halogen loss after two weeks at 175°C, (2) at least 2.5 weight-percent of halogenated polynuclear aromatic ether that (a) is halogenated with either chlorine or bromine atoms that together constitute at least 40 weight-percent of said ether, (b) exhibits less than 1 weight-percent loss when heated to 200°C in a thermogravimetric analysis performed by raising the temperature of said ether from room temperature at a rate of 40°C/minute, (c) exhibits less than about 3 weight-percent halogen loss after two weeks at 175°C, (b) exhibits less than 10 percent loss in overall weight after two weeks at 175°C, and (e) comprises less than about 50 weight-percent of said adhesive composition, and (3) antimony trioxide. A flame-retardant electrically insulating pressure-sensitive adhesive tape which is compatible, as defined herein, with magnet wire insulation and exhibits at least 20 ounces of adhesion to steel per inch of width comprising a flexible backing and at least one layer of pressure-sensitive adhesive composition united to the backing, said adhesive composition comprising an acrylate-based pressure-sensitive adhesive and 10 to 50 weight-percent of decabromodiphenyl oxide.