초록 ▼

Methods of obtaining deep through penetration of colorants into firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride compositions which comprise: applying a transfer paper or other substrate coated with a sublimable disperse dye to the surface of a firmed printable gelled plast

Methods of obtaining deep through penetration of colorants into firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride compositions which comprise: applying a transfer paper or other substrate coated with a sublimable disperse dye to the surface of a firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride composition, wherein the polyvinyl chloride resin is in particulate form having an average particle size of from about 0.5 micron to about 420 microns and contains specified percentages of plasticizer and stabilizer; applying heat thereto in the range of from about 300°F. to about 430°F. for a period of time of from about 6 seconds to about 20 seconds, whereby the sublimable disperse dye sublimes and, while in the sublimed vapor phase, penetrates deeply into the firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride composition; removing the transfer paper or other substrate, leaving the disperse dye in the firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride composition; applying a resinous polymer composition to the surface of the dyed firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride composition as a wear layer; and applying heat to the dyed firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride composition in the range of from about 310°F. to about 470°F. to fuse the polyvinyl chloride resin.

대표청구항 ▼

A method of obtaining deep through penetration into firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride compositions which comprises: applying a transfer paper or other release surface coated with a low energy, sublimable disperse dye having a molecular weight of from about 20

A method of obtaining deep through penetration into firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride compositions which comprises: applying a transfer paper or other release surface coated with a low energy, sublimable disperse dye having a molecular weight of from about 200 to about 400 to the surface of a firmed, printable gelled plastisol or sintered dry-blend polyvinyl chloride composition prepared from polyvinyl chloride resin in finely divided particulate form having a particle size of from about 0.5 micron to about 420 microns, from about 25 parts to about 150 parts of plasticizer per one hundred parts of polyvinyl chloride resin, and from about 0.4 parts to about 10 parts of a heat stabilizer per one hundred parts of polyvinyl chloride resin, said low energy, sublimable disperse dye being in direct, intimate contact with said polyvinyl chloride composition; applying heat to said polyvinyl chloride composition and said low energy sublimable disperse dye having a molecular weight of from about 200 to about 400 in the range of from about 300°F. to about 470°for a period of time of from about 6 seconds to about 20 seconds, whereby said low energy, sublimable disperse dye sublimes and, while in the vapor phase, penetrates into said firmed printable gelled plastisol or sintered dry-blend polyvinyl chloride composition and said polyvinyl chloride resin is substantially completely fused by being substantially completely solvated with said plasticizer; and removing said transfer paper or other release surface after said low energy, sublimable disperse dye has penetrated into said firmed, printable gelled plastisol or sintered dry-blend polyvinyl chloride composition and said polyvinyl chloride resin has been fused. A resinous polymer sheet material comprising: a layer of a fused polyvinyl chloride resin composition prepared from a finely divided particulate polyvinyl chloride resin having an average particle size in the range of from about 0.5 micron to about 420 microns, from about 25 parts by weight to about 150 parts by weight of a plasticizer per 100 parts by weight of said polyvinyl chloride resin, and from about 0.4 parts by weight to about 10 parts by weight of a heat stabilizer per 100 parts by weight of said polyvinyl chloride resin, said polyvinyl chloride resin being substantially completely fused by being substantially completely solvated with said plasticizer; and a colored pattern or design of a low energy sublimable disperse dye having a molecular weight of from about 200 to about 400 printed on the surface of and extending deeply through said layer of polyvinyl chloride resin composition, said colored pattern or design of a low energy sublimable disperse dye having a molecular weight of from about 200 to about 400 being formed on the underside face of a heat transfer release substrate and directly and intimately contacting the surface of said layer of a polyvinyl chloride resin composition.