초록 ▼

Thermoplastic elastomer compositions of the present invention comprise a blend of from about 10 to about 50 parts by weight of a crystalline 1-olefin polymer, from about 80 to about 15 parts by weight of a styrene-butadiene rubber, and from about 5 to about 50 parts by weight of bitumen. The thermop

Thermoplastic elastomer compositions of the present invention comprise a blend of from about 10 to about 50 parts by weight of a crystalline 1-olefin polymer, from about 80 to about 15 parts by weight of a styrene-butadiene rubber, and from about 5 to about 50 parts by weight of bitumen. The thermoplastic blends have unexpectant increases in properties, especially tear strength, tensile strength, high temperature (100° C.) tear strength, and smooth surfaces when injection molded. Moreover, the bitumen lowers the injection molding pressure, thus enabling larger parts to be molded. The compositions, which may be partially cured, also have excellent aging properties. The compositions are a true thermoplastic in that they can be repeatedly processed and yet maintain their good physical properties.

대표청구항 ▼

1. A thermoplastic elastomer composition, comprising a blend of from about 10 to about 50 parts by weight of a crystalline 1-olefin polymer, said 1-olefin polymer selected from the class consisting of a homopolymer and a copolymer made from 1-olefin monomers having from 2 to 20 carbon atoms, said

1. A thermoplastic elastomer composition, comprising a blend of from about 10 to about 50 parts by weight of a crystalline 1-olefin polymer, said 1-olefin polymer selected from the class consisting of a homopolymer and a copolymer made from 1-olefin monomers having from 2 to 20 carbon atoms, said homopolymer or said copolymer having a melting point of at least 90° C.; from about 80 to about 15 parts by weight of a random styrene-butadiene rubber; and from about 5 to about 50 parts by weight of a bitumen, said blend being partially cured in that said styrene-butadiene rubber is crosslinked to an extent less than a full cure, and having a melt flow index of at least 1.0 so that a thermoplastic elastomer is formed. 2. A thermoplastic elastomer composition according to claim 1, wherein said bitumen is an asphalt, a tar, or a tar derivative, said asphalt selected from the group consisting of a petroleum asphalt, a native asphalt, and combinations thereof, said petroleum asphalt selected from the group consisting of straight-reduced asphalts, thermal asphalts, and air-blown asphalts, said native asphalts selected from the group consisting of an asphalt with a mineral content below 5 percent, an asphalt with a mineral content above 5 percent, and combinations thereof, said tar selected from the group consisting of a coal tar reduced to float grade, a coal-tar pitch, and combinations thereof, said tar derivative being a residua from pyrogenous distillates. 3. A thermoplastic elastomer composition according to claim 2, wherein said 1-olefin homopolymer is selected from the group consisting of polyethylene and polypropylene, and wherein said 1-olefin copolymer is made from monomers of ethylene and propylene. 4. A thermoplastic elastomer composition according to claim 3 wherein the amount of said 1-olefin polymer ranges from about 30 to about 45 parts by weight, wherein the amount of said styrene-butadiene rubber ranges from about 65 to about 25 parts by weight, and wherein the amount of said bitumen ranges from about 10 to about 40 parts by weight, wherein said partial cure is obtained utilizing a compound selected from the group consisting of a sulfur curative and an organic peroxide curative, the amount of said sulfur curative ranging from about 0.01 parts to about 1.0 parts by weight per 100 parts of said blend, and wherein the amount of said organic peroxide curative ranges from about 0.01 to about 0.5 parts per 100 parts of said blend. 5. A thermoplastic elastomer composition according to claim 4, wherein said 1-olefin homopolymer is polypropylene, wherein said 1-olefin copolymer is made from a major amount by weight of propylene monomers and a minor amount by weight of ethylene monomers, wherein said bitumen is said petroleum asphalt, and wherein the melt flow index is at least 10. 6. A thermoplastic elastomer composition according to claim 5, wheein the molecular weight of said polypropylene or said copolymer ranges from about 20,000 to about 1,000,000, wherein the molecular weight of said styrene-butadiene rubber ranges from about 50,000 to about 1,000,000, wherein the softening point of said bitumen ranges from about 50° F. to about 400° F., and wherein said curative is a sulfur curative. 7. A thermoplastic elastomer composition according to claim 6, wherein the melting point of said 1-olefin polymer is at least 130° C. and wherein said curative is a sulfur curative.