초록 ▼

The present invention is concerned with the production and use of water-insoluble particulate heteropolymers made by sequential emulsion polymerization in dispersed particles of which a “core”of a polymeric base is at least partially encased in a “sheath”polymer that is permeable to an acid, such as

The present invention is concerned with the production and use of water-insoluble particulate heteropolymers made by sequential emulsion polymerization in dispersed particles of which a “core”of a polymeric base is at least partially encased in a “sheath”polymer that is permeable to an acid, such as acetic acid, adapted to cause swelling of the core by neutralization. The aqueous dispersion of the acid-swollen, base-containing core/sheath particles is useful in making water-base coating compositions, microvoids being formed in cores of the swollen particles in the film during the drying thereof. Thus, the heteropolymer dispersion can serve as an opacifying agent in coating compositions, such as water-base paints, as a supplement or replacement of part or all of the pigmentary material or extenders that would otherwise be used in such coating compositions. For convenience of description herein, the terms “core”, “sheath”, and “core/sheath polymer”are frequently used to refer to the distinct functional components of the individual polymer particles of the essential “mode”of the heteropolymers of the present invention even though in actuality, the components of the polymer particles thereof may not have the precise arrangement implied by this terminology.

대표청구항 ▼

A process for making an aqueous dispersion of water-insoluble core/sheath polymer particles comprising sequentially emulsion polymerizing at a temperature of from about 10°C. to about 100°C. in an aqueous medium containing a free radical initiator: (a) a core monomer system comprising one or more mo

A process for making an aqueous dispersion of water-insoluble core/sheath polymer particles comprising sequentially emulsion polymerizing at a temperature of from about 10°C. to about 100°C. in an aqueous medium containing a free radical initiator: (a) a core monomer system comprising one or more monoethylenically unsaturated monomers at least one of which monomers having an amine group and comprising at least 5% by weight of the core monomer system, thereby forming dispersed core particles having an average diameter of from about 0.05 to 1 micron, and (b) polymerizing in the presence of the dispersed core particles a sheath monomer system comprising at least one monoethylenically unsaturated monomer having no ionizable group to form a sheath on the core particles, any monoethylenically unsaturated amine in the sheath monomer mixture being present in an amount of no more than 10% by weight of the sheath monomers, the proportion of amine in the sheath monomer mixture being less than ⅓the proportion thereof in the core monomer mixture, the resultant core-sheath particles having an average diameter before acidification and swelling of from about 0.07 to 4.5 microns, the relative amounts of core-forming monomer(s) and sheath forming monomer(s) being such that the ratio of the weight of the core to the weight of the total polymer in the resulting dispersed particles is from about 1:4 to 1:100, said sheath being permeable to an aqueous acid and having a Ti of greater than 50°C., and (c) neutralizing with acid so as to swell said core and form particles which, when dried, contain a single void and cause opacity in compositions in which they are contained. A composition comprising an aqueous dispersion of water-insoluble core/sheath polymer particles have an average diameter of 0.07 to 4.5 microns, having a core polymerized from a monomer system comprising one or more monoethylenically unsaturated monomers, at least one of said unsaturated monomers having an amine group, and having at least one sheath polymerized from at least one different sheath monomer system, at least one of said different sheath monomer systems being hard and producing a sheath polymer having a Ti greater than 50°C., being non film-forming at 20°C., and being permeable to acid, said core being swollen by neutralization with acid in the presence of water, said particles having a property such that when subsequently dried a single cavity forms in said core and said particles cause opacity in compositions in which they are contained. Articles coated and/or impregnated with the opaque film-forming composition of claim 1.