초록

3-Hydroxybutyrate polymers are formed into oriented shaped articles by drawing a partially crystallized preform to increase at least one dimension by at least 200%, and then increasing the degree of crystallization while maintaining the drawn preform in the drawn condition.

대표청구항 ▼

1. A process for the production of an oriented shaped article from a polymer containing at least 40 mole % of 3-hydroxybutyrate residues in the polymer chain comprising uni- or bi-axially drawing a preform of said hydroxybutyrate polymer in a partially crystalline state at a temperature between the

1. A process for the production of an oriented shaped article from a polymer containing at least 40 mole % of 3-hydroxybutyrate residues in the polymer chain comprising uni- or bi-axially drawing a preform of said hydroxybutyrate polymer in a partially crystalline state at a temperature between the glass transition temperature, Tg, and the melting point of the hydroxybutyrate polymer into said shaped article, and then increasing the degree of crystallinity of the hydroxybutyrate polymer by subjecting the drawn preform, while in the drawn condition, to a temperature between the glass transition temperature and the drawing temperature until the drawn article is nonrubbery, the amount of said uni- or bi-axial drawing being such that, after said step of increasing the degree of crystallinity, at least one dimension of the preform has increased by at least 200%, said hydroxybutyrate polymer having a degree of crystallinity, at the time of drawing, such that the preform is not so brittle that it breaks before achieving said increase in said at least one dimension, and such that the drawn article does not break during the step of increasing the degree of crystallinity. 2. A process as claimed in claim 1 wherein the partially crystalline hydroxybutyrate polymer preform is produced by subjecting an amorphous HB polymer preform to a temperature within 30° C. of the temperature at which the rate of crystalisation of the hydroxybutyrate polymer is a maximum. 3. A process as claimed in claim 1 wherein the hydroxybutyrate polymer is melt extruded into the desired configuration to form an amorphous preform which is then passed through a quenching/crystallisation zone maintained at a temperature below the melting point of the hydroxybutyrate polymer to solidify the polymer and to effect the desired degree of crystallisation. 4. A process as claimed in claim 3 wherein the preform is fed directly from said quenching/crystallisation zone to the drawing stage. 5. A process as claimed in claim 1 wherein the drawing is conducted at a temperature above that at which the preform is partially crystallised. 6. A process as claimed in claim 1 wherein the drawing is conducted at a temperature between 30° and 80° C. below the melting point of the hydroxybutyrate polymer. 7. A process as claimed in claim 1 wherein the degree of crystallinity of the drawn preform is increased by subjecting the drawn preform to a temperature within 20° C. of the temperature at which the rate of crystallisation is a maximum. 8. A process as claimed in claim 1 wherein the drawn preform is allowed to relax, during the further crystallisation step, by up to 10% of the drawn value, of the at least one dimension that has been increased by at least 200% during the drawing step.