초록 ▼

A method of manufacturing a friction article wherein a fiber material (14) having a continuous and substantially uniform three dimensional matrix which is filled with a slurry (24) made up of fillers, friction modifiers, a reinforcing material and a liquid binder. The filled fiber material is convey

A method of manufacturing a friction article wherein a fiber material (14) having a continuous and substantially uniform three dimensional matrix which is filled with a slurry (24) made up of fillers, friction modifiers, a reinforcing material and a liquid binder. The filled fiber material is conveyed to a dryer (32) where the volatile solution is evaporated leaving the fillers, friction modifiers, reinforcing material and binder. The filled fiber material (14) is thereafter placed in an oven (50) where a compressive force is applied thereto while the binder is cured to define a second matrix which holds the fillers, friction modifiers, and reinforcing material in the three dimensional matrix.

대표청구항 ▼

1. A method of manufacturing a friction article for use in a brake comprising the steps of: stamping a blank having a predetermined shape from a web of open foamed material selected from a group consisting of carbon, iron, silicon carbide, nickel, and aluminum, said web having voids therein produc

1. A method of manufacturing a friction article for use in a brake comprising the steps of: stamping a blank having a predetermined shape from a web of open foamed material selected from a group consisting of carbon, iron, silicon carbide, nickel, and aluminum, said web having voids therein produced by a substantially continuous three dimensional matrix, said three dimensional matrix providing uniform structural rigidity for said blank and a conductive flow path for thermal energy; placing said blank on a conveyor; preparing a slurry made up of fillers, modifiers and a liquid binder in a volatile solution; moving said blank to a location where said slurry fills said voids to create a preformed friction article; transporting said preformed friction article to a dryer where about fifty percent of said volatile solution is removed without the formation of surface depressions caused by the release of bubbles of gas; conveying said dried preformed friction article to an oven to cure said binder and form a second matrix which holds said fillers, modifiers, and fibers in said three dimensional matrix; and applying a force to said preformed friction article during curing to produce a desired density in said friction article. 2. The method as recited in claim 1 wherein said open structure has a porosity of about 95-98% and from 14-18 pores per linear centimeter with an average pore size of 0.05 cm. 3. The method as recited in claim 1 wherein said volatile solution makes up from 30-40% by weight of the total slurry. 4. The method as recited in claim 3 wherein said slurry includes a reinforcing fiber for said second matrix selected from a group consisting of glass or metaphosphate, said fiber making up to 15% by weight of the total slurry. 5. The method as recited in claim 3 wherein said friction modifiers are selected from a group consisting of coke, iron powder, cashew nut powder, zinc and brass. 6. The method as recited in claim 5 wherein said filler is selected from a group consisting of barytes, talc, and whiting. 7. The method as recited in claim 6 wherein said liquid binder is selected from a group consisting of epoxy resins, phenolic resins, inorganic resins, silicone resins and mixtures thereof. 8. The method as recited in claim 7 wherein said dryer has a constant temperature of about 100° C. and any volatiles in said binders are removed in such a manner to prevent the formation of undesirable voids in the performed friction article. 9. The method as recited in claim 7 wherein said oven is maintained at a temperature of about 200° C. during the cure of said binder in said friction article. 10. The method as recited in claim 9 further including the step of: applying a vacuum to said fiber material to aid in filling the open structure with slurry. 11. The product produced by the method recited in claim 10.