초록 ▼

Pure silicon metal is produced from a silicon metal which contains 1-10% Ca and which is cast into molds with relatively slow rate of cooling. The cast metal is pre-crushed and thereupon subjected to a purification process consisting of two leaching steps where in the first leaching step there is em

Pure silicon metal is produced from a silicon metal which contains 1-10% Ca and which is cast into molds with relatively slow rate of cooling. The cast metal is pre-crushed and thereupon subjected to a purification process consisting of two leaching steps where in the first leaching step there is employed an aqueous solution of FeCl 3 or FeCl 3 +HCl which causes a disintegration of the metal. The fines are washed away in place thereof, and the metal is further leached in the second leaching step with an aqueous HF+HNO 3 solution. The necessary amount of calcium is supplied in the smelting furnace in the form of CaO or other suitable Ca compound.

대표청구항 ▼

1. A process for purifying metallurgical grade silicon which comprises the steps of adding one or more calcium compounds to molten metallurgical grade silicon in an amount sufficient to provide molten silicon containing about 1.0 to about 10.0% by weight of calcium, casting the molten silicon into m

1. A process for purifying metallurgical grade silicon which comprises the steps of adding one or more calcium compounds to molten metallurgical grade silicon in an amount sufficient to provide molten silicon containing about 1.0 to about 10.0% by weight of calcium, casting the molten silicon into molds and cooling the molten silicon at a sufficiently slow rate to obtain solid silicon having a grain size not over about 1.0 mm, precrushing the resulting silicon and leaching it in a first step with an aqueous solution of FeCl 3 or an aqueous solution containing FeCl 3 and HCL which cause disintegration of silicon, washing away fines from the leached silicon and in a second step leaching the silicon with an aqueous solution containing HF and HNO 3 . 2. The process of claim 1 in which the metallurgical grade silicon is produced in a smelting furnace and the one or more calcium compounds are selected from the group consisting of CaO and CaCO 3 which are added directly to the molten silicon in the smelting furnace. 3. The process of claim 1 in which the calcium compound is lime which is injected or stirred into the molten silicon. 4. The process of claim 1 which includes the step of using distilled water to wash away the fines. 5. The process of claim 1 which includes the step of substituting strontium in whole or in part for the calcium compounds set forth in claim 1.