초록

An element for selectively sensing carbon monoxide which is capable of sensing a lower concentration of CO in a quicker response time at ordinary temperatures without the need of heating the element with better SN and low temperature dependence.

대표청구항 ▼

1. A method of making a carbon monoxide sensing element comprising a first process of adding and thoroughly dispersing an aqueous chloroplatinic acid solution to stannic oxide in the range of Pt/Sn=2-10 mol % whereupon the mixture is quick frozen and dried in a vacuum, a second process of adding and

1. A method of making a carbon monoxide sensing element comprising a first process of adding and thoroughly dispersing an aqueous chloroplatinic acid solution to stannic oxide in the range of Pt/Sn=2-10 mol % whereupon the mixture is quick frozen and dried in a vacuum, a second process of adding and mixing antimony oxychloride to the product made in the first process in the range of Sb/Sn=2-8 mol %, a third process of adding an organic solvent to the product made in the second process and applying and drying the resulting paste on an insulator to which electrodes are attached and a fourth process of calcining the element made in the third process in an air atmosphere at 600° to 850° C. 2. A method of making a carbon monoxide sensing element comprising a first process of adding and thoroughly dispersing an aqueous chloroplatinic acid solution to stannic oxide in the range of Pt/Sn=2-10 mol % whereupon the mixture is quick frozen and dried in a vacuum, a second process of adding and mixing antimony oxychloride to the product made in the first process in the range of Sb/Sn=2-8 mol %, a third process of adding an organic solvent to the product made in the second process and applying and drying the resulting paste on an insulator to which an electrode is attached and a fourth process of calcining the element made in the third process in an atmosphere of previously prepared oxidizing antimony gas at 600° to 850° C. 3. A method of making a carbon monoxide sensing element according to claim 2 wherein the oxidizing antimony gas atmosphere is prepared by firing a 2×10 -9 to 3×10 -8 mol/cm 3 quantity of antimony compound calculated as a mol quantity of antimony trioxide.