초록 ▼

Sialon-base ceramic materials having both high hardness and good sinterability and can show excellent wear resistance when used in cutting tools and other wear-resisting tools. A Sialon-base ceramic material according to the invention has main components consisting of β-Sialon expressed by a chemica

Sialon-base ceramic materials having both high hardness and good sinterability and can show excellent wear resistance when used in cutting tools and other wear-resisting tools. A Sialon-base ceramic material according to the invention has main components consisting of β-Sialon expressed by a chemical formula Si 6-z Al z O z N 8-z, z being larger than 0 but not more than 4.3, and α-Sialon expressed by a chemical formula M x (Si, Al) 12 (O,N) 16, x being larger than 0 but not more than 2, M representing at least one selected from the group consisting of Li, Na, Ca, Mg, Y, and any rare earth element, the ratio of the α-Sialon/the β-Sialon being within a range from 25/75 to 95/5 in volume. The Sialon-base ceramic material further includes as a disperse phase-forming component 1-40 percent by volume at least one selected from the group consisting of carbide of Ti, Zr, or Hf, nitride thereof, carbo-nitride thereof, and carbo-oxi-nitride thereof, and as a combined phase-forming component 1-20 percent by volume at least one selected from the group consisting of oxide of any of the above M-forming elements, the above disperse phase-forming metallic elements, Si, or Al, and nitride thereof. Part of the above disperse phase-forming component (S1) may be substituted by at least one (S2) selected from the group consisting of carbide of V, Nb, Ta, or Cr, nitride thereof, carbo-nitride thereof, carbo-oxi-nitride thereof, and carbide of Mo or W, the ratio S2/(S1+S2) being within a range from 0.01 to 0.5 in volume.

대표청구항 ▼

1. A Sialon-base ceramic material consisting essentially of: (a) 1-40 percent by volume at least one dispersed phase-forming component selected from the group consisting of carbide of Ti, Zr, or Hf, nitride thereof, carbo-nitride thereof, and carbo-oxi-nitride thereof; (b) 1-20 percent by volume

1. A Sialon-base ceramic material consisting essentially of: (a) 1-40 percent by volume at least one dispersed phase-forming component selected from the group consisting of carbide of Ti, Zr, or Hf, nitride thereof, carbo-nitride thereof, and carbo-oxi-nitride thereof; (b) 1-20 percent by volume at least one combined phase-forming component selected from the group consisting of oxide of Li, Na, Ca, Mg, Y, any rare earth element, Ti, Zr, Hf, Si, or Al, and nitride thereof; and (c) the balance of β-Sialon expressed by a chemical formula Si 6-z Al z O z N 8-z, z being larger than 0 but not more than 4.3, and α-Sialon expressed by a chemical formula M x (Si, Al) 12 (O, N) 16, x being larger than 0 but not more than 2, M representing at least one selected from the group consisting of Li, Na, Ca, Mg, Y, and any rare earth element, and inevitable impurities, wherein the ratio of the α-Sialon/the β-Sialon is within a range from 25/75 to 95/5 in volume. 2. The Sialon-base ceramic material as claimed in claim 1, wherein the ratio of the α-Sialon/the β-Sialon is within a range from 30/70 to 85/15 in volume. 3. The Sialon-base ceramic material as claimed in claim 1, wherein z is larger than 0 but not more than 2.0. 4. The Sialon-base ceramic material as claimed in claim 1, wherein said at least one disperse phase-forming component is contained in an amount from 5 to 30 percent by volume. 5. The Sialon-base cermaic material as claimed in claim 1, wherein said at least one combined phase-forming component is contained in amount from 2 to 10 percent by volume. 6. The Sialon-base ceramic material consisting essentially of: (a) 1-40 percent by volume at least one dispersed phase-forming component (hereinafter referred to as S1) selected from the group consisting of carbide of Ti, Zr, or Hf, nitride thereof, carbo-nitride thereof, and carbo-oxi-nitride thereof, and at least one disperse phase-forming component (hereinafter referred to as S2) selected from the group consisting of carbide of V, Nb, Ta, or Cr, carbo-nitride thereof, carbo-oxi-nitride thereof, carbide of Mo, and carbide of W, wherein the ratio S2/(S1+S2) is within a range from 0.01 to 0.5 in volume; (b) 1-20 percent by volume at least one combined phase-forming component selected from the group consisting of oxide of Li, Na, Ca, Mg, Y, any rare earth element, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Si, or Al, and nitride thereof; and (c) the balance of β-Sialon expressed by a chemical formula Si 6-z Al z O z N 8-z, z being larger than 0 but not more than 4.3, and α-Sialon expressed by a chemical formula M x (Si, Al) 12 (O, N) 16, x being larger than 0 but not more than 2, M representing at least one selected from the group consisting of Li, Na, Ca, Mg, Y, and any rare earth element, and inevitable impurities, wherein the ratio of the α-Sialon/the β-Sialon is within a range from 25/75 to 95/5 in volume. 7. The Sialon-base ceramic material as claimed in claim 6, wherein the ratio of the α-Sialon/the β-Sialon is within a range from 30/70 to 85/15 in volume. 8. The Sialon-base ceramic material as claimed in claim 6, wherein z is larger than 0 but not more than 2.0. 9. The Sialon-base ceramic material as claimed in claim 6, wherein said S1 and S2 are contained in an amount from 5 to 30 percent by volume in total. 10. The Sialon-base ceramic material as claimed in claim 6, wherein said at least one combined phase-forming component is contained in an amount from 2 to 10 percent by volume.