초록 ▼

A polyurethane material is disclosed which is hard and has high impact strength at temperatures less than about 45° C. yet can be softened at temperatures above about 60° C. to be manually shapable. This material is obtained by reacting an araliphatic or cycloaliphatic diisocyanate with a polyol com

A polyurethane material is disclosed which is hard and has high impact strength at temperatures less than about 45° C. yet can be softened at temperatures above about 60° C. to be manually shapable. This material is obtained by reacting an araliphatic or cycloaliphatic diisocyanate with a polyol component which contains at least 50 wt % of a polyether obtained predominantly from propylene oxide. The polyol component has a number average molecular weight between about 350 and 1000 and an OH number between about 250 and 600. The reaction is conducted at an NCO to OH ratio of between about 0.75:1 and 1.25:1. This material finds utility in the medical field, particularly in forming orthopedic devices, in model construction, as a protective coating, as an impression material, as a decorative material or as a glazing material.

대표청구항 ▼

1. A polyurethane constructional material which is hard and has high impact strength at temperatures below about 45° C. but is softened to a manually shapable state by exposure to temperatures in excess of about 60° C. comprising the reaction product of a) an isocyanate component comprising at le

1. A polyurethane constructional material which is hard and has high impact strength at temperatures below about 45° C. but is softened to a manually shapable state by exposure to temperatures in excess of about 60° C. comprising the reaction product of a) an isocyanate component comprising at least one diisocyanate which: i) contains at least one cycloaliphatic or aromatic residue in its molecular structure; and ii) has both of its isocyanate groups bound to other than an aryl carbon atom; with b) a polyol component comprising at least one polyether which: i) is built up predominantly from propylene oxide units; ii) has a number average molecular weight of between about 350 and 1000; and iii) has an OH number between about 250 and 600, said reaction product being synthesized using an NCO to OH ratio of between about 0.75:1 and 1.25:1. 2. The material of claim 1 wherein the NCO to OH ratio used in synthesizing the reaction product is between about 0.9:1 and 1.1:1. 3. The material of claim 1 wherein the isocyanate component also contains biuretized, trimerized or carbodiimidized diisocyanate. 4. The material of claim 1 wherein at least one diisocyanate is selected from the group consisting of isophorone diisocyanate, dicyclohexane-4,4'-diisocyanate, xylylene diisocyanate and mixtures thereof. 5. The material of claim 1 or 2 or 3 or 4 wherein the polyol component is a polyether comprising at least about 60 mol percent of propylene oxide residues. 6. The material of claim 5 wherein the polyether comprises at least about 80 mol percent propylene oxide residues. 7. The material of claim 1 or 2 or 3 or 4 wherein the polyol component is a polyether started on an initiator selected from the group consisting of propylene glycol, glycerol, trimethylol propane, pentaerythritol, sorbitol and mixtures thereof. 8. The material of claim 7 wherein the polyether comprises at least about 60 mol percent propylene oxide residues. 9. The material of claim 8 wherein the polyether comprises at least about 80 mol percent propylene oxide residues. 10. The material of claim 1 or 2 or 3 or 4 wherein the polyether (a) has a number average molecular weight of between about 400 and 800; and (b) has an OH number between about 350 and 450. 11. The material of claim 10 wherein the polyether comprises at least about 60 mol percent of propylene oxide residues. 12. The material of claim 1 or 2 or 3 or 4 wherein the polyol component comprises a mixture of polyethers which give the mixture the average properties of (a) a number average molecular weight between about 350 and 1000; and (b) an OH number between about 250 and 600. 13. The material of claim 12 wherein (a) the number average molecular weight is between about 400 and 800; and (b) the OH number is between about 350 and 450. 14. The material of claim 1 or 2 or 3 or 4 wherein (a) up to about 500 mol percent of the polyol component comprises hydroxyl bearing compounds other than polyethers; and (b) the polyol component has: (i) a number average molecular weight of between about 350 and 1000; and (ii) an average OH number between about 250 and 600. 15. The material of claim 14 wherein (a) the number average molecular weight is between about 400 and 800; and (b) the OH number is between about 350 and 450. 16. The polyurethane constructional material which is hard and has high impact strength at temperatures below about 45° C. but is softened to a manually shapable state by exposure to temperatures in excess of about 60° C. comprising the reaction product of (a) a diisocyanate selected from the group consisting of isophorone diisocyanate, dicyclohexane-4,4'-diisocyanate, xylylene diisocyanate and mixtures thereof, and (b) at least one polyether (i) comprising at least about 80 mol percent of propylene oxide residues; (ii) started on an initiator selected from the group consisting of propylene glycol, glycerol, trimethylol propane, pentaerythritol, sorbitol and mixtures thereof; (ii) having a number average molecular weight between about 400 and 800; and (iv) having an OH number between about 350 and 450, said reaction product being synthesized using an NCO to OH ratio of between about 0.9:1 and 1.25:1. 17. A process for the preparation of a polyurethane constructional material which is hard and has a high impact strength at temperatures below about 45° C. but is softened to a manually shapable state by exposure to temperatures in excess of about 60° C. comprising reacting (a) an isocyanate component comprising at least one diisocyanate which: (1) contains at least one cycloaliphatic or aromatic residue in its molecular structure; and (2) has both of its isocyanate groups bound to other than an aryl carbon atom; with (b) a polyol component comprising (1) at least one polyether which (i) is built up predominantly from propylene oxide units; (ii) has a number average molecular weight of between about 350 and 1000; and (iii) has an OH number between about 250 and 600; and (2) optionally up to 50 wt. percent, based on the total weight of the polyol component, of other OH bearing compounds so selected that the polyol component has on average (i) number average molecular weight between about 350 and 1000; and (ii) an OH number between about 250 and 600, said reaction being conducted in one or several stages such that the overall NCO to OH ratio is between about 0.75:1 and 1.25:1 under conditions suitable for the formation of a polyurethane. 18. A process for the formation of an orthopedic device comprising (a) forming a material which is hard and has high impact strength at temperatures below about 45° C. but is softened to a manually shapable state by exposure to temperatures above about 60° C. in accordance with claim 17; (b) heating or maintaining the material obtained from step (a) at a temperature above about 60° C. until it is shaped to the desired configuration; and (c) allowing the shaped material to cool to below about 45° C. 19. A process for the preparation of rigid plastic articles having good impact strength and displaying hardness similar to that obtainable from homopolymers of methyl methacrylate comprising (a) forming a material which is hard and has high impact strength at temperatures below about 45° C. but is softened to a manually shapable state by exposure to temperatures above about 60° C. in accordance with claim 17; (b) forming this material into the desired configuration at a temperature above about 60° C.; and (c) allowing the shaped material to cool to below about 45° C. 20. The process of claim 19 wherein the material is transparent and is utilized as a glazing material. 21. The process of claim 19 wherein the material is formed by impressing it with a rigid article. 22. The process of claim 19 wherein the material is formed into a decorative configuration. 23. The process of claim 19 wherein the material is formed into a model of a larger or smaller article. 24. The process of claim 19 wherein the material is formed into a protective covering. 25. A process for the formation of an orthopedic device comprising (a) forming a material which is hard and has a high impact strength at temperatures below 45° C. but is softened to a manually shapable state by exposure to temperatures above 60° C. by reacting (I) an isocyanate component comprising at least one diisocyanate which: (i) contains at least one cycloaliphatic or aromatic residue in its molecular structure; and (ii) has both of its isocyanate groups bound to other then an aryl carbon atom; with (II) a polyol component comprising: (i) at least one polyether which is built up predominantly from polypropylene oxide units, has a number average molecular weight from about 350 and 1000, and has an OH number between about 250 and 600; (ii) optionally up to 50 weight percent, based on the total weight percent of the polyol component, of other OH bearing compounds so selected that the polyol component has an average number average molecular weight between 350 and 1000; and an OH number between 250 and 600, said reaction being conducted in one or several stages such that the overall NCO:OH ratio is between about 0.75:1 and 1.25:1 under conditions suitable for the formation of a polyurethane, (b) casting this reaction mixture into the form of a sheet, (c) heating this sheet material to a temperature in excess of 60° C., (d) conforming this heated sheet material to the portion of the human or animal body to be supported or immobilized by the orthopedic material, (e) allowing this conformed material to cool down to a temperature below 45° C., and affixing or securing the cooled sheet material to the body portion to which it has been conformed.