초록 ▼

A carbonaceous material, such as crushed coal, is admixed or impregnated with an inexpensive alkali metal compound, such as sodium chloride, and then pretreated with a stream containing steam at a temperature of 350° to 650° C. to enhance the catalytic activity of the mixture in a subsequent gasific

A carbonaceous material, such as crushed coal, is admixed or impregnated with an inexpensive alkali metal compound, such as sodium chloride, and then pretreated with a stream containing steam at a temperature of 350° to 650° C. to enhance the catalytic activity of the mixture in a subsequent gasification of the mixture. The treatment may result in the transformation of the alkali metal compound into another, more catalytically active, form.

대표청구항 ▼

1. A process for the in situ formation of a gasification catalyst in a carbonaceous material which comprises: (a) mixing an alkali metal halide with said carbonaceous material; (b) thereafter treating said mixture in a stream containing steam at a temperature of 350° to 650° C. for a sufficient

1. A process for the in situ formation of a gasification catalyst in a carbonaceous material which comprises: (a) mixing an alkali metal halide with said carbonaceous material; (b) thereafter treating said mixture in a stream containing steam at a temperature of 350° to 650° C. for a sufficient time period to hydrolyze at least 25 mole% of said alkali metal to form a hydrolyzed product in the substantial absence of any gasification to enhance the catalytic activity of the resultant mixture in subsequent gasification of said mixture; (c) utilizing high pressure steam at a high space velocity to remove the HCl gas as it is formed in said hydrolysis reaction; and (d) passing the resultant gasification catalyst product to a gasification zone. 2. The process of claim 1 wherein said carbonaceous material is in particulate form. 3. The process of claim 2 wherein said carbonaceous material is selected from the class consisting of coal, coke, carbon, char, charcoal, and biomass. 4. The process of claim 2 wherein said alkali metal compound is mixed with said particulate carbonaceous material in a slurry. 5. The process of claim 2 wherein said alkali metal halide is dissolved in a liquid and said particulate carbonaceous material is then soaked in said liquid to treat said carbonaceous material with said alkali metal halide. 6. The process of claim 5 wherein said carbonaceous material is soaked in said liquid for at least 10 minutes. 7. The process of claim 5 wherein said alkali metal halide solution is sprayed on said carbonaceous material. 8. The process of claim 2 wherein said metal halide is in particulate form and said alkali metal halide and said particulate carbonaceous material are mixed together to form a particulate mixture. 9. The process of claim 1 wherein the pressure of said steam is from 2 to 300 atmospheres. 10. The process of claim 1 wherein the mole ratio of alkali metal to carbon is from 0.02 to 0.2. 11. The process of claim 2 wherein said stream containing steam comprises one or more gases selected from the class consisting of steam, a steam-oxygen mixture, a steam-air mixture, and a steam-nitrogen mixture. 12. The process of claim 1 wherein said alkali metal halide comprises a halogen salt of sodium and said hydrolyzed product is selected from the class consisting of sodium hydroxide, sodium oxide, and mixtures thereof. 13. A process for the in situ formation of a gasification catalyst in a carbonaceous material which comprises: (a) pretreating a particulate carbonaceous material having a particle size of 8 mesh or smaller with sodium chloride in a mole ratio of from 0.02 to 0.2 sodium to carbon; (b) exposing said sodium chloride-carbonaceous mixture to a stream containing steam at a temperature of from 350° to 650° C., a pressure of from 2 to 300 atmospheres, and for a time period sufficient to hydrolyze at least 25 mole% of said sodium in the substantial absence of any gasification to thereby form in situ the corresponding alkali metal hydroxide or oxide catalyst having enhanced catalytic activity; and (c) passing the resultant gasification catalyst product to a gasification zone. 14. The process of claim 12 wherein said halogen salt of sodium comprises sodium chloride. 15. A process for the production of an inexpensive gasification catalyst for the production of gases from carbonaceous materials which comprises: (a) impregnating a porous particulate carbonaceous material having a particle size of 8 mesh or less with a solution containing sodium chloride in a mole ratio of from 0.02 to 0.2 sodium to carbon; (b) reacting said mixture with steam at a temperature of from 350° to 650° C., a pressure of from 2 to 300 atmospheres, and for a time period sufficient to hydrolyze at least 25 mole% of said sodium in the substantial absence of any gasification; (c) removing hydrogen chloride gas from said mixture as it is formed; and (d) passing the resultant gasification catalyst product to a gasification zone.