초록 ▼

Lightweight nonwoven sheets of polyethylene plexifilamentary film-fibril strands are made by a stretching-and-bonding operation in which the unit weight of the sheet is decreased in stages while at a temperature within 3° to 8° C. of the melting point of the polyethylene. The resultant sheet has a n

Lightweight nonwoven sheets of polyethylene plexifilamentary film-fibril strands are made by a stretching-and-bonding operation in which the unit weight of the sheet is decreased in stages while at a temperature within 3° to 8° C. of the melting point of the polyethylene. The resultant sheet has a novel combination opacity, X-ray scattering and physical characteristics and is particularly suited for sterile packaging, lightweight envelopes and surgical drapes.

대표청구항 ▼

1. In a wide, lightweight, bonded, non-woven sheet of polyethylene plexifilamentary film-fibril strands having a unit weight of no greater than 60 g/m2, the improvement comprising in combination, an opacity of at least 75% and a pattern of long wavelength X-ray scattering which is characterized by a

1. In a wide, lightweight, bonded, non-woven sheet of polyethylene plexifilamentary film-fibril strands having a unit weight of no greater than 60 g/m2, the improvement comprising in combination, an opacity of at least 75% and a pattern of long wavelength X-ray scattering which is characterized by a Guinier plot of the logarithm of the intensity of the scattered X-rays versus the square of the scattering angle, said plot exhibiting a ratio of the slope at 0.005 square radians to the slope at 0.010 square radians that is no greater than 0.85. 2. A sheet of claim 1 wherein the sheet weighs no more than 50 g/m 2, the slope ratio is no greater than 0.80 and the opacity is at least 80%. 3. A sheet of claim 1 or 2 wherein the sheet weighs no more than 35 g/m 2 . 4. A sheet of claim 1 or 2 wherein the sheet has a bacterial inhibition rate of at least 75% and a Gurley-Hill permeability in the range of 0.8 to 4.8 sec/100 cm 3 /cm 2 . 5. A sheet of claim 1 or 2 wherein the sheet weighs no more than 35 g/m 2, has a slope ratio of no greater than 0.75, an opacity of no less than 85%, a bacterial inhibition rate of at least 90%, a delamination strength of at least 0.3 N/cm, a Gurley-Hill permeability of at least 1.4 sec/100 cm 3 /cm 2 and a hydrostatic head of at least 150 cm. 6. In a process for preparing a wide lightweight, bonded non-woven sheet of flash-spun polyethylene plexifilamentary film-fibril strands, which process includes the steps of forming a lightly consolidated, non-bonded sheet of such strands, the improvement comprising heating the formed sheet without significant stretching to a temperature that is in the range of 3° to 8° C. below the melting point of the polyethylene, then while being maintained at said temperature, stretching the sheet in at least two stages to at least 1.2 times its original length to provide a sheet weighing no more than 60 g/m 2, then cooling the sheet to a temperature of less than 60° C., and during the heating, stretching and cooling, while the sheet is at a temperature of at least 100° C., applying forces perpendicular to the surface of the sheet to restrain the sheet from shrinking transversely by more than 10%. 7. A process of claim 6 wherein the sheet is heated to a temperature in the range of 127° to 133° C. and then is stretched in no more than four stages at a stretch rate of no greater than 2×10 4 %/min to 1.3 to 2.5 times its original length. 8. A process of claim 7 wherein the temperature is in the range of 128° to 132° C., the stretch rate is no greater than 5×10 3 %/min and the resultant stretched sheet is between 1.5 and 2.0 times its original length. 9. A process of claim 6 or 7 wherein the cooling to a temperature of less than 60° C. is accomplished by applying the cooling first through one surface and then through the opposite surface of the sheet.