초록 ▼

Improved stable crosslinked dispersion which is further stabilized with butylated melamine formaldehyde resin. The dispersion to which the improvement of the invention applies is formed by addition polymerization of selected monomers in the presence of an organic liquid which is a solvent for the mo

Improved stable crosslinked dispersion which is further stabilized with butylated melamine formaldehyde resin. The dispersion to which the improvement of the invention applies is formed by addition polymerization of selected monomers in the presence of an organic liquid which is a solvent for the monomers, but a non-solvent for the polymer and a polymeric dispersion stabilizer having solvated and non-solvated segments.

대표청구항 ▼

1. A stable crosslinked dispersion containing microgel particles, said dispersion being: (i) formed by addition polymerization of (a) between about 1 and about 10 mole percent each of first and second ethylenically unsaturated monomers, each bearing functionality capable of crosslinking reactio

1. A stable crosslinked dispersion containing microgel particles, said dispersion being: (i) formed by addition polymerization of (a) between about 1 and about 10 mole percent each of first and second ethylenically unsaturated monomers, each bearing functionality capable of crosslinking reaction with the other, and (b) between about 80 and about 98 mole percent of at least one other monoethylenically unsaturated monomer in the presence of (I) a hydrocarbon dispersing liquid which is a solvent for the polymerizable monomers, but a non-solvent for the resultant polymer, and (II) polymeric dispersion stabilizer containing at least two segments, with one segment being solvated by said dispersing liquid and the second segment being of different polarity than said first segment and relatively insoluble in said dispersing liquid, wherein the reaction is carried out at elevated temperature such that the dispersion polymer first forms and then is crosslinked; and (ii) stabilized further by inclusion therein of a further stabilizer which, except for solvent, consists essentially of butylated melamine formaldehyde resin have a number average molecular weight in the range of about 700 to about 2,500, said further stabilizer being included in said crosslinked dispersion in an amount ranging from about 25 to about 75 parts of resin solids per 100 parts total resin solids in said crosslinked dispersion. 2. A crosslinked dispersion in accordance with claim 1 wherein said further stabilizer is included in said crosslinked dispersion in an amount ranging from about 40 to about 60 parts of resin solids per 100 parts of total resin solids in said crosslinked dispersion. 3. A crosslinked dispersion in accordance with claim 1 wherein said crosslinked dispersion including said further stabilizer contains between about 30 and about 70 percent solids. 4. A stable crosslinked dispersion in accordance with claim 1 wherein said polymeric dispersion stabilizer is a graft copolymer containing two polymeric segments, with one segment being solvated by said dispersing liquid and the second segment being an anchor polymer of different polarity than said first segment and relatively non-solvatable by said dispersing liquid, and wherein said polymeric dispersion stabilizer contains pendent groups which have been addition copolymerized with the ethylenically unsaturated monomers in the copolymerization process. 5. A stable crosslinked dispersion in accordance with claim 4 wherein said polymeric dispersion stabilizer is formed by graft copolymerizing the reaction product of glycidyl methacrylate and poly(12-hydroxystearic acid) with methylmethacrylate and glycidyl methacrylate and then reacting the resulting copolymer product containing pendent epoxy groups with methacrylic acid. 6. A stable crosslinked dispersion in accordance with claim 1 wherein the functionalities of said first and second ethylenically unsaturated monomers used to form the dispersed polymer of said dispersion respectively are selected from the group consisting of: (a) acid and epoxide; (b) epoxide and amine; (c) acid anhydride and hydroxyl; (d) acid anhydride and amine; (e) acid anhydride and mercaptan; (f) isocyanate and hydroxyl; (g) hemiformal and amide; (h) carbonate and amine; (i) cycloimide and amine; (j) cycloimide and hydroxyl; and (k) imine and alkoxysilane. 7. A stable crosslinked dispersion in accordance with claim 6 wherein said dispersion liquid is an aliphatic hydrocarbon solvent and said first and second ethylenically unsaturated monomers (a) and said at least one other ethylenically unsaturated monomer (b) used in the preparation of said dispersed polymer are acrylic monomers. 8. A stable crosslinked dispersion in accordance with claim 6 wherein said dispersion is formed by free radical addition copolymerization in the presence of hydrocarbon dispersing liquid of from about 2 to about 5 mole percent of alpha, beta ethylenically unsaturated monocarboxylic acid, from about 90 to about 96 mole percent of at least one other copolymerizable monoethylenically unsaturated monomer and from about 2 to about 5 mole percent of crosslinking monomer selected from the group consisting of ethylenically unsaturated monoepoxides. 9. A stable crosslinked dispersion in accordance with claim 8 wherein said monomers used in the addition copolymerization to form said dispersed polymer are characterized in that said alpha, beta ethylenically unsaturated monocarboxylic acid is methacrylic acid, said other copolymerizable monoethylenically unsaturated monomer is methylmethacrylate and said crosslinking monomer is glycidyl methacrylate. 10. A stable crosslinked dispersion containing microgel particles said dispersion being: (i) formed by addition polymerization of between about 1 and about 10 mole percent of alpha, beta ethylenically unsaturated monocarboxylic acid, from about 80 to about 98 mole percent of at least one other copolymerizable monoethylenically unsaturated monomer and from about 1 to about 10 mole percent of crosslinking monomers selected from the group consisting of ethylenically unsaturated monoepoxides, in the presence of (I) a hydrocarbon dispersing liquid which is a solvent for the polymerizable monomers, but a non-solvent for the resultant polymer, and (II) polymeric dispersion stabilizer containing at least two segments, with one segment being solvated by said dispersing liquid and the second segment being of different polarity than said first segment and relatively insoluble in said dispersing liquid, said polymeric dispersion stabilizer being formed by graft copolymerizing the reaction product of glycidyl methacrylate and poly(12-hydroxystearic acid) with methylmethacrylate and glycidyl methacrylate and reacting the resulting copolymer product containing pendent epoxy groups with methacrylic acid, wherein the reaction is carried out at elevated temperatures such that the dispersion polymer first forms and then is crosslinked; and (ii) stabilized further by inclusion therein of a further stabilizer which, except for solvent, consists essentially of butylated melamine formaldehyde resin have a number average molecular weight in the range of about 700 to 2,500, said further stabilizer being included in said crosslinked dispersion in an amount ranging from about 25 to about 75 parts of resin solids per 100 parts of total resin solids in said crosslinked dispersion. 11. A stable crosslinked dispersion in accordance with claim 10 wherein said further stabilizer is included in said crosslinked dispersion in an amount ranging from about 40 to about 60 parts resin solids per 100 parts of total resin solids in said crosslinked dispersion. 12. A stable crosslinked dispersion in accordance with claim 10 wherein said crosslinked dispersion including said further stabilizer contains between about 30 and about 70 percent solids. 13. A stable crosslinked dispersion in accordance with claim 10 wherein said further stabilizer consists essentially of a solution of butylated melamine formaldehyde resin in organic solvent in an amount such that the percentage solids of said butylated melamine formaldehyde resin in said hydrocarbon solvent ranges from about 50 to about 90 percent. 14. A stable crosslinked dispersion in accordance with claim 13 wherein said further stabilizer consists essentially of a 65 percent solids solution of said butylated melamine formaldehyde resin in a 2/1 solution of butylacetate and butyl alcohol.