초록 ▼

A reinforced refractory product having increased tensile strength is provided comprising a refractory material such as a phosphate bonded castable refractory having distributed therein ceramic fibers in yarn form consisting of roved bundles of filaments. A method of distributing the ceramic fibers i

A reinforced refractory product having increased tensile strength is provided comprising a refractory material such as a phosphate bonded castable refractory having distributed therein ceramic fibers in yarn form consisting of roved bundles of filaments. A method of distributing the ceramic fibers in the refractory is also provided wherein a mix of water and refractory material matrix is first formed and thereafter the fibers are added. Such method substantially reduced the risk of fiber damage during incorporation of the fiber in the matrix.

대표청구항 ▼

1. A reinforced refractory product comprising a refractory material having ceramic fibers in yarn form in an approximate percentage by weight of the total in a range from 0.25 to 1.0 distributed therein, said fibers being in yarn form for the purpose of enhancing the modulus of rupture of said produ

1. A reinforced refractory product comprising a refractory material having ceramic fibers in yarn form in an approximate percentage by weight of the total in a range from 0.25 to 1.0 distributed therein, said fibers being in yarn form for the purpose of enhancing the modulus of rupture of said product. 2. The product of claim 1 wherein said refractory material is a phosphate bonded castable refractory. 3. The product of claim 1 wherein said ceramic fibers are comprised of an alumina-boria-silicate composition. 4. The product of claim 3 wherein said ceramic fibers comprise 62% alumina, 14% boria and 24% silica by weight. 5. The product of claim 1 wherein said ceramic fibers are comprised of filaments having a filament tensile strength of at least about 250,000 p.s.i. 6. The product of claim 5 wherein said filaments have an average diameter of about 11 microns. 7. The product of claim 1 wherein said fibers are sized with an organic polymeric material. 8. The product of claim 7 wherein sadi organic polymeric material is polytetrafluoroethylene. 9. A reinforced refractory product of enhanced modulus of rupture at temperatures of between approximately 1000° F. to 1600° F., comprising a phosphate-bonded castable refractory having ceramic fibers in yarn form distributed therein in an approximate percentage by weight of the total in a range from 0.25 to 1.0. 10. The product of claim 9 wherein said fibers are comprised of an alumina-boria-silicate composition. 11. The product of claim 10 wherein said fiber comprises 62% alumina, 14% boria and 24% silicate. 12. The product of claim 9 wherein said yarn formed of said ceramic fibers comprises roved bundles of filaments. 13. The product of claim 12 wherein said filaments have an average diameter of about 11 microns. 14. The product of claim 12 wherein said filaments have a tensile strength of at least about 250,000 p.s.i. 15. The product of claim 9 wherein said ceramic fibers in yarn form are sized with polytetrafluoroethylene. 16. A reinforced refractory product comprising a phosphate-bonded castable refractory having ceramic fibers distributed therein, said fibers being a yarn comprised of roved bundles of filaments of an alumina-boria-silicate composition in approximate percent by weight of the total in a range from 0.25 to 1.0. 17. The product of claim 16 wherein said fibers are comprised of 62% alumina, 14% boria and 24% silica. 18. The product of claim 16 wherein said filaments have a filament tensile strength of at least about 250,000 p.s.i. 19. The product of claim 16 wherein said filaments have an average diameter of 11 microns. 20. The product of claim 16 wherein said fibers are sized with polytetrafluoroethylene. 21. A method of forming a product of ceramic fibers in yarn form in a refractory material, comprising the steps of: (a) forming a mix of a refractory matrix and water; and (b) blending said ceramic fibers in yarn form in approximate percentage by weight of the total in a range from 0.25 to 1.0, with said mix until said fibers are dispersed therein. 22. The method of claim 21 wherein said refractory material is a phosphate bonded castable refractory. 23. A method of forming a product of enhanced modulus of rupture comprising ceramic fibers in yarn form in a refractory material, comprising the steps of: (a) adding water to a refractory matrix to form a mix having a plastic consistency; and (b) adding and blending said ceramic fibers in yarn form in approximate weight of the total in a range from 0.25 to 1.0, with said mix until said fibers are dispersed therein. 24. The method of claim 23 wherein said refractory material is a phosphate bonded castable refractory. 25. The method of claim 24 wherein said blending step is performed about two minutes after adding said water. 26. The method of claim 24 wherein said blending occurs for one minute after adding said fibers. 27. A method of forming a product of enhanced modulus of rupture comprising ceramic fibers in yarn form in a refractory material, comprising the steps of: (a) adding a quantity of water to a refractory matrix with water sufficient to form a mix having a plastic consistency; (b) adding said ceramic fibers in yarn form in an approximate percentage by weight of the total in a range from 0.25 to 1.0, to said mix about two minutes after adding said water; and (c) blending said fibers with said mix for about one minute. 28. The method of claim 27 wherein said refractory is a phosphate bonded castable refractory.