초록 ▼

An aqueous flocculant solution containing a tannin based polymer compound is produced which is stable and has a shelf life of at least 3-6 months before gelling. The solution is made by reacting at a temperature of from 150°-200° F. a tannin, an amino compound, and an aldehyde under slightly acidic

An aqueous flocculant solution containing a tannin based polymer compound is produced which is stable and has a shelf life of at least 3-6 months before gelling. The solution is made by reacting at a temperature of from 150°-200° F. a tannin, an amino compound, and an aldehyde under slightly acidic conditions where the pH is less than 7 and where the molar ratio of the primary amine from the amino compound to the tannin repeating unit is from about 1.5:1 to 3.0:1. The intermediate viscosity of the reaction mixture is monitored until the reaction mixture has an intermediate viscosity within the range of the system key intermediate viscosity range. This system key intermediate viscosity range is previously determined for each reactant system to be employed. It is a narrow intermediate viscosity range that is experimentally determined which permits the resulting product to have a long shelf life. The narrow system key intermediate viscosity range will generally be within the range of from about 2-100 cps when measured at 180° F. on a Brookfield LVT viscometer. When this viscosity is reached, the reaction is terminated and the solids content of the liquid is adjusted to about 20% to 60% by weight and the pH is adjusted to a value of less than 3.0.

대표청구항 ▼

1. A method of forming an aqueous solution of a tannin based polymer compound suitable for use as a flocculant comprising the steps of (a) forming an aqueous reaction mixture of a tannin, an amino compound, and an aldehyde under slightly acidic conditions where the pH is less than 7 and where the

1. A method of forming an aqueous solution of a tannin based polymer compound suitable for use as a flocculant comprising the steps of (a) forming an aqueous reaction mixture of a tannin, an amino compound, and an aldehyde under slightly acidic conditions where the pH is less than 7 and where the molar ratio of the primary amine from the amino compound to the tannin repeating unit is from about 1.5:1 to 3.0:1; (b) heating the reaction mixture at a temperature of from about 150°-200° F. until the reaction product forms which has an intermediate viscosity within the range of the system key intermediate viscosity range, said system key intermediate viscosity range being determined for each reactant system as the narrow intermediate viscosity range which permits the resulting product to have a long shelf-life, said system key intermediate viscosity range being within the range of from about 2-100 cps when measured at 180° F. on a Brookfield LVT viscometer, and (c) terminating the reaction when the intermediate viscosity has reached the condition specified in step (b) and adjusting the solids content of the liquid to about 20 to 60% by weight and adjusting the pH to a value of less than 3.0. 2. The method according to claim 1, wherein the amino compound is monoethanolamine. 3. The method according to claim 1, wherein the aldehyde is formaldehyde. 4. The method according to claim 3, wherein the amino compound is monoethanolamine. 5. The method according to claim 1, wherein the temperature in step (b) is about 175°-185° F. 6. The method according to claim 1, wherein the amino compound is an amine and the primary amine to tannin repeating unit molar ratio is from about 1.7:1 to 2.0:1. 7. The method according to claim 1, wherein the tannin is provided in the form of a quebracho powder. 8. The method according to claim 7, wherein the amino compound is monoethanolamine and the aldehyde is formaldehyde. 9. The method according to claim 8, wherein the reaction temperature is about 175°-185° F., the intermediate viscosity is about 38-40 cps, the final solids content is about 35 to 45 weight % and the pH is about 1.7 to 2.6. 10. The method according to claim 9, wherein the solids content in step (c) is adjusted to about 40 to 45% by weight. 11. The method according to claim 9, wherein the pH of the reaction product in step (c) is adjusted to about 2.3 to 2.6. 12. The product made by the process of claim 1. 13. The product made by the process of claim 9. 14. The method according to claim 1, wherein the amino compound is selected from the group consisting of methylamine, dimethylamine, trimethylamine, and mixtures thereof. 15. The method according to claim 14, wherein the reaction temperature is about 175°-185° F., the intermediate viscosity is about 4-15 cps, the final solids content is about 38-32 weight percent and the pH is about 1.7 to 2.6. 16. The method according to claim 15, wherein the pH is about 1.9. 17. The product made by the process of claim 14. 18. The product made by the process of claim 15. 19. A stable aqueous solution of a tannin based polymer compound formed by reacting tannin, an amino compound and an aldehyde under slightly acidic conditions where the pH is less than 7, said solution having a solids content of 20 to 60% by weight, a pH of less than 3, and having a stable shelf life such that it remains a liquid and does not gel at ambient conditions for at least 3 months. 20. In a process of treating wastewater by the addition of a flocculant, the improvement wherein the flocculant is the aqueous solution of a tannin based polymer compound of claim 19. 21. In a process of treating wastewater by the addition of a flocculant, the improvement wherein the flocculant is the aqueous solution of a tannin based polymer compound of claim 12. 22. In a process of treating wastewater by the addition of a flocculant, the improvement wherein the flocculant is the aqueous solution of a tannin based polymer compound of claim 13. 23. In a process of treating wastewater by the addition of a flocculant, the improvement wherein the flocculant is the aqueous solution of a tannin based polymer compound of claim 17. 24. In a process of treating wastewater by the addition of a flocculant, the improvement wherein the flocculant is the aqueous solution of a tannin based polymer compound of claim 18.