초록 ▼

A process for coating a polymer surface with a hydrophilic coating with low friction in wet condition. The process comprises applying to the polymer surface a solution containing between 0.05 to 40% of a compound which comprises at least two unreacted isocyanate groups per molecule, evaporating the

A process for coating a polymer surface with a hydrophilic coating with low friction in wet condition. The process comprises applying to the polymer surface a solution containing between 0.05 to 40% of a compound which comprises at least two unreacted isocyanate groups per molecule, evaporating the solvent, applying a solution containing between 0.5 to 50% of polyvinylpyrrolidone to the thus treated polymer surface and then evaporating the solvent of the last mentioned solution, and curing the coating at elevated temperature. The process is preferably carried out in the presence of a catalyst for the curing of isocyanate.

대표청구항 ▼

A process for placing on a polymer surface a hydrophilic coating which has a low coefficient of friction when wetted with a water-based liquid, which consists essentially of applying to the polymer surface a solution which consists essentially of an organic solvent and between 0.05 to 40% (weight to

A process for placing on a polymer surface a hydrophilic coating which has a low coefficient of friction when wetted with a water-based liquid, which consists essentially of applying to the polymer surface a solution which consists essentially of an organic solvent and between 0.05 to 40% (weight to volume) of an isocyanate monomer having at least two unreacted isocyanate groups per molecule, or an isocyanate pre-polymer thereof having up to 5 monomer units, or a mixture of such monomers and pre-polymers, evaporating the solvent, applying a second solution consisting essentially of a solvent between 0.5 to 10% (weight to volume) of polyvinylpyrrolidone containing an amine catalyst in an amount between 0.1 and 50% by weight to the thus treated polymer surface and then evaporating the solvent of the second solution, and curing the coating in the presence of a water-containing gas at elevated temperature; and, wherein said polymer is selected from the group consisting of rubber, latex rubber, vinylpolymers, polyesters, and polyacrylates.