초록 ▼

A thin-walled work piece of plastics material is cast in a mold by pouring or flowing the plastics material in the form of a plastisol or a flowable powder into a preheated casting mold which is locked to a casting container in a sealed manner to form a closed casting cavity. The mold and the contai

A thin-walled work piece of plastics material is cast in a mold by pouring or flowing the plastics material in the form of a plastisol or a flowable powder into a preheated casting mold which is locked to a casting container in a sealed manner to form a closed casting cavity. The mold and the container are then lifted or rotated through at least 180°. A reduced pressure is maintained in the cavity at least prior and during the tilting. After a predetermined time the reduced pressure is removed and the mold and container are tilted back into the starting position. The mold and container are then separated again and the mold is then heated for completion of the jelling or curing whereupon the mold is cooled for removing the work piece from the mold.

대표청구항 ▼

A method for casting thin-walled work pieces of synthetic material, comprising the following steps: (a) preheating a casting mold (2), (b) maintaining a quantity of flowable powder of synthetic material in a casting container (3) substantially to a predetermined filling level, (c) closing the castin

A method for casting thin-walled work pieces of synthetic material, comprising the following steps: (a) preheating a casting mold (2), (b) maintaining a quantity of flowable powder of synthetic material in a casting container (3) substantially to a predetermined filling level, (c) closing the casting container (3) with the preheated casting mold (2) to form a liquid and pressure tight casting unit enclosing a casting cavity (13), (d) beginning to vibrate the casting unit and evacuating the casting cavity to a reduced pressure while the casting unit is vibrating, said reduced pressure being just sufficient to remove air from said casting cavity but also insufficient to suck said flowable powder out of said casting cavity, (e) rotating the casting unit in one direction through 180°from a mold-up starting position into a mold-down casting position, and providing a dwell time for permitting said flwoable powder of synthetic material to move into said preheated casting mold in the mold-down position, further rotating said casint unit in the same direction back to the starting mold-up position, providing a dwell time in said starting mold-up position, and then rotating the casting unit in the opposite direction again in two steps of 180°each with a dwell time at the casting position and at the starting position for uniformly covering the casting mold surfaces with a powder layer of substantially uniform thickness throughout, (f) said dwell times permitting the flowable powder of synthetic material to begin to form a jelled skin on the inner surface of said preheated casting mold, (g) permitting any excess flowable powder of synthetic material to move back into said casting container when said casting unit is in the last mentioned mold-up position, (h) removing the casting mold from the casting container and moving the casting mold into a heating station for curing the work piece which has formed as said jelled skin on the internal surfaces of the casting mold, and (i) after curing, cooling the casting mold and removing the work piece from the casting mold.