초록 ▼

A process for preparing a solid, water absorbing, cross-linked polyacrylate resin including combining potassium acrylate and a polyvinyl monomer, such as N,N-methylene bisacrylamide, with water in an amount of 55 to 80 combined weight percent of potassium acrylate and polyvinyl monomer based on the

A process for preparing a solid, water absorbing, cross-linked polyacrylate resin including combining potassium acrylate and a polyvinyl monomer, such as N,N-methylene bisacrylamide, with water in an amount of 55 to 80 combined weight percent of potassium acrylate and polyvinyl monomer based on the total weight of potassium acrylate, polyvinyl monomer and water to form a monomer mixture, and adding a polymerization initiator to the monomer mixture to initiate polymerization of the monomer mixture. The monomer mixture then is polymerized without external heating by utilizing the exothermic heat of reaction as substantially the only non-ambient energy source to drive water away from said polyacrylate resin to form the cross-linked polyacrylate resin having a water content sufficiently low (i.e. 15% or less) to be powdered, such as by pulverization, without an intermediate drying step.

대표청구항 ▼

A process for preparing a solid, water absorbing, cross-linked resin comprising: combining a monomer mixture of (A) potassium acrylate; and (B) a water miscible or water soluble polyvinyl monomer, with water in an amount of 55 to 80 combined weight percent of (A) plus (B) based on the total weight o

A process for preparing a solid, water absorbing, cross-linked resin comprising: combining a monomer mixture of (A) potassium acrylate; and (B) a water miscible or water soluble polyvinyl monomer, with water in an amount of 55 to 80 combined weight percent of (A) plus (B) based on the total weight of (A) plus (B) plus water to form a monomer mixture wherein the monomers of the monomer mixture consist essentially of (A) and (B); adding a polymerization initiator to said monomer mixture capable of initiating, and in an amount sufficient to initiate polymerization of said monomer mixture; depositing said monomer mixture including said initiator onto a support surface in sheet form for polymerization and cross-linking; and polymerizing said monomer mixture while utilizing the exothermic heat of reaction as substantially the only non-ambient energy source to drive water away from said polyacrylate resin to form said cross-linked polyacrylate resin having a water content sufficiently low to be powdered without an intermediate drying step.