An effective autodeposition bath with low volatile organic compound emissions can be compounded with polymer solids made by polymerizing a mixture of monomers consisting of certain acrylates and other monomers. E.g., a suitable mixture is, in percents by weight, 44% butyl acrylate, 36% acrylonitrile

An effective autodeposition bath with low volatile organic compound emissions can be compounded with polymer solids made by polymerizing a mixture of monomers consisting of certain acrylates and other monomers. E.g., a suitable mixture is, in percents by weight, 44% butyl acrylate, 36% acrylonitrile, 10% styrene, 7% methacrylic acid, 2% of the methyl ether of methacrylamide, and 1.5% of hydroxyethyl acrylate.

대표청구항 ▼

A process for coating ferriferous or zinciferous or both zinciferous and ferriferous surfaces, said process comprising steps of: (1) contacting said surfaces with an aqueous liquid autodeposition composition comprising dispersed polymer solids, an acidic component, and an oxidizer component for a ti

A process for coating ferriferous or zinciferous or both zinciferous and ferriferous surfaces, said process comprising steps of: (1) contacting said surfaces with an aqueous liquid autodeposition composition comprising dispersed polymer solids, an acidic component, and an oxidizer component for a time sufficient to cause formation of an adherent coating on said surfaces; (2) withdrawing the surfaces coated in step (A) from contact with the autodeposition and maintaining the surfaces coated in step (A) in contact with a gaseous atmosphere containing water vapor for a selected dwell time; (3) rinsing the dwelled coated surfaces from step (2) with substantially pure water for a specified rinse time; (4) contacting the coated, dwelled, and rinsed surface from step (3) with a chromium containing post-treatment composition for a specified post-treatment time; and (5) curing the post-treated coated surface by exposure to gases at a temperature of at least about 140°C. for a specified cure time, so as to produce an adherent dry coating on the surface, wherein the improvement comprises selecting the dispersed polymer solids so that they consist essentially of one or more copolymers made by polymerizing a homogeneous mixture of monomers by addition polymerization, said homogenous mixture of monomers consisting essentially of: (A) from about 40-about 50 of monomers selected from the group having the general formula I: [Figure] (I) where R1 is a saturated, branched or unbranched, alkyl group having from about 3 to about 8 carbon atoms and R2 is hydrogen or methyl; (B) from about 30-about 40 w/o of acrylonitrile; (C) from 0-about 20 w/o of monomers selected from the group consisting of styrene, a5-about 10 w/o of monomers selected from the group consisting of acrylic acid and methacrylic acid; (E) from 0-about 5 w/o of the methyl ether of methyl acrylamidoglycolate, having chemical formula II [Figure] (II) (F) from 0-about 5 w/o of monomers selected from the group having the general chemical formula III [Figure] (III) where R2 has the same meaning as in part (A) and R3 is a saturated, branched or unbranched, divalent hydrocarbon moiety having from 2 to 4 carbon atoms and having its two open valences on distinct carbon atoms.