초록 ▼

Ultra strong lightweight core material capable of sustained operation at unusually high temperatures for composite structure of the type used in aircraft parts such as wings, fairings and stabilizers is produced from preimpregnated thermoplastic fibercloth ribbon by the manufacturing processes of th

Ultra strong lightweight core material capable of sustained operation at unusually high temperatures for composite structure of the type used in aircraft parts such as wings, fairings and stabilizers is produced from preimpregnated thermoplastic fibercloth ribbon by the manufacturing processes of this invention. The fibercloth ribbon is preformed between corrugated rollers of a special roll forming press which heats the ribbon to a softening temperature, forms it into a pattern of half-hex corrugations, cools it and sets it in that pattern. Then sheets cut from the corrugated ribbon are stacked into a bonding press along with hex forming mandrels placed between the sheets in the corrugations. With a full stack, the press is enclosed with side covers containing heating units, hydraulic pressure is applied to compress and consolidate the stack and contact interfacial facets, and heat is applied by directing superheated air jets on the mandrel ends until a bonding temperature is reached, forming the material accurately around the hex mandrels and fusion bonding adjacent sheets together at interfacial facets in a honeycomb pattern. After cooling to a setting temperature, pressure is removed and the bonded stack is removed from the bonding press. The mandrels are then extracted in a special long stroke thin pin pneumatic press, yielding a finished block of lightweight core material having a honeycomb pattern of hex ducts with rigid walls.

대표청구항 ▼

A method for forming a fiber reinforced honeycomb structure of open cells from a ribbon of thermoplastic resin impregnated fibercloth, said resin having a softening temperature, comprising: providing a pair of forming wheels mounted for rotation to lie in the same plane with their outer perimeters t

A method for forming a fiber reinforced honeycomb structure of open cells from a ribbon of thermoplastic resin impregnated fibercloth, said resin having a softening temperature, comprising: providing a pair of forming wheels mounted for rotation to lie in the same plane with their outer perimeters touching at a tangent, each wheel having teeth of mating shape and corrugated for meshing together; heating one of the wheels to above the softening temperature of said thermoplastic resin while maintaining the other wheel at a temperature substantially below said softening temperature; training said ribbon between said wheels in full contact with said other wheel around a substantial arc thereon so that said ribbon makes contact with said heated wheel solely at the region of mesh between said wheels whereat it is softened and shaped by the contact forces between the wheels into a corrugated form and is thereafter immediately cooled by contact with said other wheel as it continues to travel along said arc in contact with said other wheel to form a shaped ribbon; cutting the shaped ribbon into sheets; stacking a plurality of shaped mandrels along with a plurality of said sheets configured in a manner to uniformly surround and separate each of said mandrels and to form a stack having a systematic matrix pattern of said corugations; applying pressure to said entire stack, thereafter applying heat to said stack so as to thermal fusion bond the thermoplastic material together into a ducted pattern conforming to said corrugated shape and maintained by said mandrels; thereafter cooling said stack and removing the pressure therefrom; and thereafter extracting said mandrels from said stack to leave a ducted core structured in said systematic matrix pattern.